| 牌号简介 About |
|---|
| 符合ISO 1043-1的材料规范：用40%重量%长的玻璃纤维增强的PP紫外线稳定聚丙烯，低排放。纤维与聚丙烯基体发生化学耦合。球是圆柱形的，通常也包括10 mm长的嵌入纤维。Celstran成型件具有高强度、高刚度、高热变形等优异的力学性能。由于部件中内置了纤维骨架，因此在高温和低温下缺口冲击强度会增加。长纤维增强能显著降低蠕变。模制品的各向同性收缩使翘曲最小化。通过注射成型，可以制造出具有高再现性的复杂零件。应用领域：汽车功能/结构件 Material code according to ISO 1043-1: PP UV-stabilized polypropylene reinforced with 40 weight percent long glass fibers, low emission. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive |
产品描述 Product Description
用途：汽车领域的应用;
加工条件：注射成型 Injection Molding
性能特点： 机械强度好; 化学耦合; 低VOC; 耐低温冲击; 各向同性好; 低翘曲性; 耐候抗UV; 韧性好; Good Rigidity,Weather resistance is good,Low warping,Good flexibility,Low odor,Chemical coupling,low-temperature impact resistance,Good Isotropy
紫外线：UV Stabilized
填料：玻璃纤维 40
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.22 | g/cm³ | ISO 1183 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
9200 | MPa | ISO 527-2/1A |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
130 | MPa | ISO 527-2/1A/5 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
2.0 | % | ISO 527-2/1A/5 |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
9000 | MPa | |
|
80℃ 80℃ |
MPa | ||
|
弯曲强度 bending strength |
|||
|
23℃ 23℃ |
MPa | ||
|
80℃ 80℃ |
MPa | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
-30℃ -30℃ |
kJ/m² | ||
|
23℃ 23℃ |
kJ/m² | ||
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
-30℃ -30℃ |
kJ/m² | ||
|
23℃ 23℃ |
kJ/m² | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
8.0 MPa，未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
|
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
| 备注 |
|---|
| 2. 10°C/min |
|
【新闻资讯】查看全部
taulman 3D公司推出高强度PETG基资料
2016-07-20 以不断推出创新的高性能线材而知名的taulman 3D公司在今年推出了独特的高强度PETG基材料guidel!ne，应用在医疗设备领域中。该材料符合ISO 10993的国际生物相容标准，并且具有卓越的高温打印功能。一般来说，由于热堆积的原因，打印部分零件的细小特征会比较困难。guidel!ne更不易受这些散热问题的影响，从而能够打印出更精细且不失真的细节。guidel!ne原材料已通过特定的FDA 测试并在FDA中列出。 taulman 3D公司表示，guidel!ne将仅 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付