LXSAN FL2000是一种中等流动性的聚碳酸酯(PC)树脂,用于结构发泡成型,允许在0.24(6mm)壁上减轻各种重量。该产品具有低温冲击强度和高耐热性,与Lexan FL2000树脂结合使用,仅提供不透明颜色。 LEXAN FL2000 is a medium flow specialty polycarbonate (PC) resin for structural foam molding, allowing for various weight reductions at 0.24" (6.0mm) wall. This product offers low temperature impact strength and high heat resistance in combination with LEXAN FL2000 resin is available in opaque colors only. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- 3 |
1.09 | g/cm³ | |
-- -- |
1.21 | g/cm³ | |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
10 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:6.4 mm MD:6.4 mm |
0.60 到 0.80 | % | 内部方法 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.13 | % | |
平衡,23℃ Equilibrium, 23 ℃ |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
6.40 mm 6.40 mm |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服,6.35 mm Yield, 6.35 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,6.35 mm Fracture, 6.35 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
6.40 mm 6.40 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服,6.40 mm Yield, 6.40 mm |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃,6.4 mm 23℃,6.4 mm |
J/m | ASTM D4812 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
-40℃,Total Energy -40℃,Total Energy |
J | ||
-20℃,Total Energy -20℃,Total Energy |
J | ||
跌落标靶冲击 Falling target impact |
|||
23℃ 23℃ |
J | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~95℃ MD:-40~95℃ |
1/℃ | ASTM E831 | |
比热 specific heat |
J/kg/℃ | ASTM C351 | |
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电常数 Dielectric constant |
|||
100 Hz 100 Hz |
|||
1 MHz 1 MHz |
|||
耗散因数 Dissipation factor |
|||
100 Hz 100 Hz |
|||
1 MHz 1 MHz |
|||
耐电弧性 Arc resistance 4 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) 5 |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
3.90 mm 3.90 mm |
|||
6.00 mm 6.00 mm |
|||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
Flame Class Minimum Density(Foam) Flame Class Minimum Density(Foam) |
g/cm³ | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Weight Reduction Weight Reduction |
|||
Foam - Electrical:6.40 mm Foam - Electrical:6.40 mm |
% | ||
Foam - Impact:6.40 mm Foam - Impact:6.40 mm |
% | ||
Foam - Mechanical:6.40 mm Foam - Mechanical:6.40 mm |
% | ||
Foam - Physical:6.40 mm Foam - Physical:6.40 mm |
% | ||
Foam - Thermal:6.40 mm Foam - Thermal:6.40 mm |
% |
备注 |
---|
3. Foam Molded |
4. 钨电极 |
5. Surface |
【新闻资讯】查看全部
科思创取得企业社会责任优秀案例奖
2016-08-02 全球领先的聚合物生产商科思创近日在上海荣获“绿色发展 共享未来”企业社会责任(CSR)优秀案例奖。该评选在上海市政府的支持下进行,肯定了科思创为建立环保、安全、高效的物流网络所作出的不懈努力。该奖项使科思创成为了一个范例,启发其他企业如何将可持续发展的原则转化成切实可行的工作,以促进自身业务的发展。 “我们非常荣幸能获得这个奖项。科思创的物流网络彰显了我们是如何在每一项工作中贯彻‘人类、环境、盈利’的可持续发展定位。”科思创大中华区公关传媒、政府事务及可持续发展总监魏晓安表 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |