牌号简介 About |
---|
Onflex-HT热塑性弹性体化合物是基于氢化苯乙烯嵌段共聚物。这一系列的化合物是专门配制的,以在高温和高耐热性下提供非常好的压缩永久变形性能。此外,Onflex HT化合物具有优异的机械性能、较宽的硬度范围和良好的加工性能。提高紫外线稳定性 OnFlex™ HT thermoplastic elastomer compounds are based on hydrogenated styrenic block copolymers. This range of compounds is specially formulated to deliver very good compression set performance at elevated temperatures and a high heat resistance. Furthermore, OnFlex™ HT compounds offer excellent mechanical properties, a wide hardness range and good processability. Improved UV stability |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,10 秒 Shore A, 10 seconds |
70 | ISO 7619 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 |
|||
TD,断裂 TD, fracture |
12.0 | MPa | |
MD,断裂 MD, fracture |
9.50 | MPa | |
拉伸应变 Tensile strain 3 |
|||
TD,断裂 TD, fracture |
950 | % | |
流量,断裂 Flow rate, fracture |
700 | % | |
撕裂强度 tear strength |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
|||
23℃,72 hr 23℃,72 hr |
% | ||
70℃,22 hr 70℃,22 hr |
% | ||
100℃,22 hr 100℃,22 hr |
% | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
耐候性 Weathering resistance 4 |
内部方法 | ||
通用材料类型 Common material types |
|||
|
|||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
收缩率 Shrinkage rate 2 |
|||
MD:2.0 mm,注塑成型 MD: 2.0 mm, injection molded |
% | ||
TD:2.0 mm,注塑成型 TD: 2.0 mm, injection molding |
% | ||
熔体表观粘度 Apparent viscosity of melt |
|||
200℃,1340 sec^-1 200℃,1340 sec^-1 |
Pa·s | ||
200℃,11200 sec^-1 200℃,11200 sec^-1 |
Pa·s |
备注 |
---|
2. Sign convention: Positive shrinkage factor: Ejected part is smaller than the mould cavity. Shrinkage after processing is dependent on tool design, wall thickness and processing conditions. Due to the multitude of factors influencing shrinkage during the processing users should only treat this as a guide and should make their own assessment. Generally, low processing temperatures will cause an increase in shrinkage of up to 1% (direction of flow). Part geometry may further influence shrinkage by gradually releasing strain. This may be accelerated by the annealing of parts, such as for 1hr at 80 °C. |
3. 200 mm/min |
4. UV-Package succesfully tested acc. to PV 3929 (Kalahari-Test) on a 60 Sh A Version. |
【新闻资讯】查看全部
金融管理部门密集发声 三“稳”信号明确
2022-04-27 继4月25日晚间宣布下调外汇存款准备金率之后,4月26日盘前,中国人民银行有关负责人就当前金融市场情况接受媒体采访,回应经济形势、应对疫情影响、规范平台经济、实施货币政策 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |