| 牌号简介 About |
|---|
| LEXAN EXL1182T聚碳酸酯（PC）硅氧烷共聚物树脂是一种紫外线稳定，增强释放透明注塑（IM）级。与标准PC树脂相比，该树脂具有良好的低温（20 C）延展性、高流动性和良好的加工性，有机会缩短IM循环时间。Lexan Exl118T树脂是一种紫外线稳定的增强型释放产品，有透明和不透明的颜色可供选择，是广泛应用的理想选择。 LEXAN EXL1182T polycarbonate (PC) siloxane copolymer resin is a UV stabilized, enhanced release transparent injection molding (IM) grade. This resin offers good low temperature (-20 C) ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC resins. LEXAN EXL1182T resin is a UV stabilized, enhanced release product available in transparent and opaque colors and may be an excellent candidate for a broad range of applications. |
产品描述 Product Description
用途：电气/电子应用领域;电子显示器;
加工条件：注射成型 Injection Molding
性能特点： 共聚物; 成型周期快; 机械强度好-延展; 流动性高; 耐候抗UV; 易加工; Weather resistance is good,Excellent Processability,High liquidity,Ductility,Quick molding cycle,Copolymer
紫外线：UV Stabilized
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.19 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
20 | g/10min | ASTM D1238 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
300℃，1.2 kg 300℃，1.2 kg |
19.0 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
0.40 到 0.80 | % | 内部方法 |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
0.24 | % | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
-- -- 3 |
MPa | ASTM D638 | |
|
-- -- |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield 4 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
断裂 fracture 4 |
MPa | ASTM D638 | |
|
断裂 fracture |
MPa | ISO 527-2/50 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield 4 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/50 | |
|
断裂 fracture 4 |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/50 | |
|
弯曲模量 Bending modulus |
|||
|
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
|
-- -- 6 |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
-- -- 6 , 7 |
MPa | ISO 178 | |
|
屈服，50 mm跨度 Yield, 50 mm span 5 |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength 8 |
|||
|
-30℃ -30℃ |
kJ/m² | ||
|
23℃ 23℃ |
kJ/m² | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
-30℃ -30℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
-30℃ -30℃ 9 |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ 9 |
kJ/m² | ISO 180-1A | |
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
23℃，Total Energy 23℃，Total Energy |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火，4.0 mm，64 mm跨距 1.8 MPa, unannealed, 4.0 mm, 64 mm span 9 |
℃ | ISO 75-2/Af | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
-- -- |
℃ | ASTM D1525 10 | |
|
B120 B120 |
℃ | ISO 306/B120 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：-40~95℃ MD：-40~95℃ |
1/℃ | ASTM E831 | |
|
MD：23~80℃ MD：23~80℃ |
1/℃ | ISO 11359-2 | |
|
TD：-40~95℃ TD：-40~95℃ |
1/℃ | ASTM E831 | |
|
TD：23~80℃ TD：23~80℃ |
1/℃ | ISO 11359-2 | |
| 备注 |
|---|
| 3. 50 mm/min |
| 4. 类型 1, 50 mm/min |
| 5. 1.3 mm/min |
| 6. 2.0 mm/min |
| 7. at Yield |
| 8. 80*10*4 sp=62mm |
| 9. 80*10*4 mm |
| 10. 速率 A (50°C/h), 压 力1 (10N) |
|
【新闻资讯】查看全部 
中国石油化工勘察设计协会完成新一届任期，袁学民等五人当选为轮值
2022-07-26 7月22日，中国石油化工勘察设计协会第八届会员代表大会第一次会议和第八届理事会第一次会议在北京举行。会议以线上+线下的形式举行，有300多名代表出席。协会的新任期圆满结束。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付