牌号简介 About |
---|
HANWHA LLDPE 3305采用滚圆工艺制造,设计用于通用薄膜。LLDPE 3305具有良好的机械性能和加工性能的平衡性。 HANWHA LLDPE 3305 is manufactured by Spherilene process and designed for general purpose film. LLDPE 3305 has well balanced property of mechanical property and processability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.922 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.9 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
30 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
断裂 fracture |
17.7 | MPa | ASTM D638 |
MD,断裂,30 µm MD, fracture, 30 µ m |
37.3 | MPa | ASTM D882 |
TD,断裂,30 µm TD, fracture, 30 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
断裂 fracture |
% | ASTM D638 | |
MD,断裂,30 µm MD, fracture, 30 µ m |
% | ASTM D882 | |
TD,断裂,30 µm TD, fracture, 30 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
30 µm 30 µm |
g | ASTM D1709 | |
撕裂强度 tear strength |
ASTM D1004 | ||
MD,30 µm MD,30 µm |
kN/m | ASTM D1004 | |
TD,30 µm TD,30 µm |
kN/m | ASTM D1004 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融峰值温度 Melting peak temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
30 µm 30 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
2016年台北国际塑橡胶工业展亮点不断
2016-08-29 两年一次的台北国际塑橡胶工业展览会 (TaipeiPLAS),自1987年首届举办以来,今年已经是第15届,目前稳居台湾第一大的塑橡胶专业展。本届TaipeiPLAS共有533家厂商参展,除了台湾332家、中国大陆34家厂商外,更有来自德、美、土耳其、日本、印度、新加坡、泰国及越南等14国企业参展,展出面积达48,000平方米,使用摊位数较上届增长36%,再创新高。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |