| 牌号简介 About |
|---|
| HWB-1051是一种经认证的优质己烯共聚物高分子量产品，开发用于高性能中大型工业容器的吹塑成型。HWB-1051具有加工性好、熔融强度好、ESCR结合性好、冲击强度高、刚度好、热成型性好、耐化学性好等特点。HWB-1051应用包括20至55加仑的容器、化学和汽油罐、手提箱、汽车零件、工具箱、卡车床内衬以及板材、管道和型材挤压。HWB-1051建议的加工温度为190至210°C。HWB-1051符合FDA法规21CFR 177.1520（c）3.1（a）+3.2（a）以及大多数与食品接触使用聚乙烯的国际法规。 HWB-1051 is a certified prime grade Hexene copolymer High Molecular Weight developed for BLOW MOLDING of high performance medium to large size industrial containers. HWB-1051 features good processability, good melt strength, excellent combination of ESCR, high Impact strength, Stiffness, good Thermoform ability, and good chemical resistance. HWB-1051 applications include 20 to 55 gallon containers, chemical and gasoline tanks, carrying cases, automotive parts, tool boxes, truck-bed liners, and sheet, pipe and profile extrusion. HWB-1051 recommended processing temperature is 190 to 210°C.. HWB-1051 complies with FDA regulation 21CFR 177.1520 (c )3.1(a) + 3.2 (a) and with most international regulations concerning the use of Polyethylene in contact with food articles. |
产品描述 Product Description
用途：汽车领域的应用;衬里;片材;型材;工具/零件箱;工业容器;管道系统;油箱;
加工条件：吹塑成型
性能特点： 熔体强度好; 机械强度好; 共聚物; 耐化学性; 己烯共聚单体; 冲击性能好; 食品接触; 抗应力开裂; 易加工; Good Rigidity,Excellent Processability,High impact resistance,Food contact compliance,Good melt strength,Copolymer,Solvent resistance,Hexene copolymers,High ESCR
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.951 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
|
190℃，2.16kg 190℃，2.16kg |
0.060 | g/10min | ASTM D1238 |
|
190℃，21.6kg 190℃，21.6kg |
10 | g/10min | ASTM D1238 |
|
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
|
模压成型，F50 Molded into shape, F50 |
> 1000 | hr | ASTM D1693 |
|
50 ℃，1.75 mm，10%非离子表面活性剂，模压成型，F50 50 ℃, 1.75 mm, 10% non-ionic surfactant, molded, F50 |
150 | hr | ASTM D1693B |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength 1 |
|||
|
屈服，模压成型 Yield, molding 1 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain 1 |
|||
|
断裂，模压成型 Fracture, molded 1 |
% | ASTM D638 | |
|
弯曲模量 Bending modulus 2 |
|||
|
1% 正割，模压成型 1% cut, molded 2 |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸冲击强度 Tensile impact strength |
|||
|
模压成型 Compression Molding |
kJ/m² | ASTM D1822 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
吹气模制温度 Blowing molding temperature |
℃ | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2.0 in/min |
| 3 0.051 in/min |
|
【新闻资讯】查看全部
2016新年完毕 钛白粉市场3月或将续涨
2016-02-24 2月进入下旬，节后的钛白粉价格市场相对比较平稳，市场多数货源充足，正月十五已过，2016的新年已基本结束，下游部分企业需求正在逐渐苏醒，预计元宵节过后大部分下游企业或陆续开工，需求或得以带动，农历新年前的第二次调涨巩固第一次调价成果意味较浓，3月随着市场的逐步打开，市场价格或再涨，幅度在300元/吨左右。目前国内多数硫酸法金红石型和锐钛型钛白粉的主流报价在9500-10600元/吨和8300-9500元/吨(均含税)，价格跨度增大。生意社化工分社钛白粉分析师杨逊认为：钛白粉2月节后的行情主 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付