| 牌号简介 About |
|---|
| Lexan 923x树脂Lexan923x是一种紫外线稳定高流动冲击改性注射成型（IM）牌号。该树脂提供基于无溴、无氯阻燃系统的UL94 V0@1.5毫米阻燃性能、低温延展性和良好的加工性能，与标准PC相比，具有更短的IM循环时间。Lexan 923x树脂是一种可用于各种不透明颜色的产品，可能是一种很好的候选材料。 LEXAN923x is a UV stabilized high flow impact modified injection molding (IM) grade. This resin offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, low temperature ductility characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN 923x resin is a product available in a wide range of opaque colors and may be an excellent candidate for a wide range of applications. |
产品描述 Product Description
用途：通用;
颜色：不透明,可用颜色
加工条件：注射成型 Injection Molding
性能特点： 无卤; 防火阻燃等级V-0; 成型周期快; 机械强度好-延展; 流动性高; 阻燃; 防火阻燃等级5VA; 冲击性能好; 耐候抗UV; 易加工; Weather resistance is good,Excellent Processability,High impact resistance,High liquidity,Ductility,Quick molding cycle,Halogen free,Flame Characteristics,V-0,5VA
紫外线：UV Stabilized
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.19 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
16 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
0.40 到 0.80 | % | 内部方法 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 3 |
2100 | MPa | ASTM D638 |
|
拉伸强度 tensile strength 4 |
ASTM D638 | ||
|
屈服 yield |
58.0 | MPa | ASTM D638 |
|
断裂 fracture |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain 4 |
ASTM D638 | ||
|
屈服 yield |
% | ASTM D638 | |
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus 5 |
|||
|
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 5 |
|||
|
屈服，50 mm跨度 Yield, 50 mm span 5 |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
-30℃ -30℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
23℃，Total Energy 23℃，Total Energy |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 6 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM E831 | ||
|
MD：-40~40℃ MD：-40~40℃ |
1/℃ | ASTM E831 | |
|
TD：-40~40℃ TD：-40~40℃ |
1/℃ | ASTM E831 | |
|
相对温度指数 Relative temperature index |
℃ | UL 746 | |
|
电气性能 Electrical performance |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
3.00 mm 3.00 mm |
UL 94 | ||
|
灼热丝可燃性指数 Glowing wire flammability index |
|||
|
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
|
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
|
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.20 in/min |
| 3 类型 1, 2.0 in/min |
| 4 0.051 in/min |
| 5 标准 B (120°C/h), 载荷2 (50N) |
|