牌号简介 About |
---|
PURPRENE A88 BK10是一种热稳定的PP/EPDM基热塑性硫化弹性体(TPV)。这种黑色化合物主要用于发动机罩下和内部应用,可以使用注塑、挤压、吹塑或其他熔融加工技术进行加工。产品以1000磅盖洛德包装箱或55磅包装袋中的自由流动颗粒形式提供。 PURPRENE A88 BK10 is a heat stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV). This black compound is intended primarily for under the hood and interior applications and can be processed using Injection Molding, Extrusion, Blow Molding or other melt processing techniques. Product is supplied as free flowing pellets in 1000 Lb. Gaylord boxes or 55 pound bags. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 到 1.00 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
5.0 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,5 秒 Shore A, 5 seconds |
84 到 92 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412A | ||
TD,100% 应变 TD, 100% strain |
> 5.60 | MPa | ASTM D412A |
MD,100% 应变 MD, 100% strain |
> 6.00 | MPa | ASTM D412A |
拉伸强度 tensile strength |
ASTM D412A | ||
TD,屈服 TD, yield |
MPa | ASTM D412A | |
MD,屈服 MD, yield |
MPa | ASTM D412A | |
拉伸应变 Tensile strain |
ASTM D412A | ||
TD,断裂 TD, fracture |
% | ASTM D412A | |
流量,断裂 Flow rate, fracture |
% | ASTM D412A | |
撕裂强度 tear strength 2 |
ASTM D1004 | ||
TD TD |
kN/m | ASTM D1004 | |
MD MD |
kN/m | ASTM D1004 | |
压缩形变 Compression deformation |
|||
125℃,70 hr 125℃,70 hr |
% | ASTM D395B | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ASTM D573 | ||
135℃,1000 hr 135℃,1000 hr |
% | ASTM D573 | |
100% 应变,135℃,1000 hr 100% strain, 135 ℃, 1000 hr |
% | ASTM D573 | |
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
100% 应变,150℃,168 hr 100% strain, 150 ℃, 168 hr |
% | ASTM D573 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
ASTM D573 | ||
135℃,1000 hr 135℃,1000 hr |
% | ASTM D573 | |
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
ASTM D573 | ||
邵氏 A,135℃,1000 hr Shaw A, 135 ℃, 1000 hr |
ASTM D573 | ||
邵氏 A,150℃,168 hr Shaw A, 150 ℃, 168 hr |
ASTM D573 | ||
拉伸强度的变化率 The rate of change in tensile strength |
ASTM D471 | ||
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
100% 应变,125℃,70 hr,在IRM 903油中 100% strain, 125 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
极限伸长率的变化率 Change rate of ultimate elongation |
|||
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
体积变化 Volume change |
|||
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
撕裂强度的变化率 Change rate of tear strength |
|||
70 hr,in IRM 903 Oil,125℃ 70 hr,in IRM 903 Oil,125℃ |
% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾化 atomization |
% | SAE J1756 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色稳定性 Color stability |
|||
Delta E Delta E |
|||
耐臭氧性 Ozone resistance 3 |
|||
Rating,40℃ Rating,40℃ 3 |
ISO 1431-1 | ||
氙老化测试 Xenon aging test 4 |
|||
Surface Defects Surface Defects 4 |
SAE J1885 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 IRM 903, 70 hrs |
4 100 pphm |
5 1240.8kJ/m² |
【新闻资讯】查看全部
美国制造业回归将对中国模具行业形成一定影响
2016-12-05 美国作为以服务型经济为主的国家,其科研开发能力、技术创新能力都是全球顶尖的。当前美国提出重夺制造业大国的口号,正在积极发展制造业。随着中国近两年劳动力成本的升高,美国制造业回归更显得理所当然。 对于美国制造业回归对中国模具行业造成的影响,业内人士表示,截止目前还未对模具行业产生多大影响,中国模具企业仍然有自己的成本优势。美国模具企业如果在当地生产模具,成本仍然很高,但是把模具设计发给中国企业做会节省不少成本。但是从长远看,美 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |