| 牌号简介 About |
|---|
| 产品描述：SABIC® LDPE HP2023J是一种低密度聚乙烯级，采用防滑和防堵添加剂配制而成。它通常表现出更好的下拉能力和高输出。薄膜具有良好的光学特性，低摩擦和低阻塞。典型应用：薄膜收缩膜、层压膜、食品和工业品包装膜、袋和袋。它还可以在不卡住的情况下实现高速转换。本产品不适用于医疗和制药应用。 PRODUCT DESCRIPTION: SABIC® LDPE HP2023J is a Low Density Polyethylene grade formulated with slip and anti-block additives. It typically exhibits better draw down ability with high output. Films typically have good optics with low friction and low blocking. TYPICAL APPLICATIONS: Thin shrink film, lamination film, packaging films for food and industrial goods, bags & pouches. It also enables high speed converting without sticking. This product is not intended for use in medical and pharmaceutical applications. |
产品描述 Product Description
用途：薄膜;包装;袋子;工业应用;收缩性薄膜;食品包装;层压板;
加工条件：吹塑薄膜
性能特点： 抗结块性; 高光滑性; 易剥离; 食品接触; 低摩擦系数; 低密度; 光学性能; Smoothness,Good dissection,Optical performance,Low coefficient of friction,High anti-blocking,Food contact compliance,Low density
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.923 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
2.0 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
0.05 mm 0.05 mm |
260 | MPa | ISO 527-2 |
|
摩擦系数 friction coefficient |
< 20 | % | ISO 8295 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
50 | µm | |
|
薄膜厚度 film thickness |
|||
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
屈服，0.05 mm Yield, 0.05 mm |
MPa | ISO 527-2 | |
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，50 µm，吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
|
TD，断裂，50 µm，吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
|
落锤冲击 Drop hammer impact |
|||
|
50 µm，吹塑薄膜 50 µ m, blow molded film |
g | ASTM D1709 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
|||
|
A50 A50 |
℃ | ISO 306/A50 | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | ISO 3146 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
ASTM D2457 | ||
|
20°，50 µm，吹塑薄膜 20 °, 50 µ m, blow molded film |
ASTM D2457 | ||
|
60°，50.0 µm，吹塑薄膜 60 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
50 µm，吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Blow（up Ratio） Blow（up Ratio） |
|||
| 备注 |
|---|
| 1 Natural Silica |
| 2 Erucamide |
| 3 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
投资意向不低于100亿元，厦钨新能拟投建锂离子正极材料项目
2021-09-17 搜料网资讯： 厦钨新能公告，公司与雅安经济技术开发区管理委员会于9月16日签署《锂离子正极材料项目投资意向书》。公司计划在雅安经开区投资建设锂离子正极材料项目，预计投资 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付