CALIBRE™ 200-14聚碳酸酯树脂是一种天然的、符合FDA标准的、14熔体流动速率的通用聚碳酸酯树脂,不含脱模剂或紫外线稳定剂。政府和行业标准:美国FDA 21 CFR 177.1580 CSA保险商实验室(UL)欧盟食品接触2002/72/EC应用食品处理器饮料容器食品用具其他包装应用 CALIBRE™ 200-14 polycarbonate resin is a natural, FDA compliant, 14 melt flow rate general purpose polycarbonate resin with no mold release or UV stabilizer. Govt. and Industry Standards: U.S. FDA 21 CFR 177.1580 CSA Underwriters Laboratory (UL) EU food contact 2011/10/EC Applications Food processors Beverage containers Food utensils Other packaging applications |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
密度 Density |
1.20 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
14 | g/10min | ISO 1133 |
300℃,1.20kg 300℃,1.20kg |
14 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
12.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
% | ISO 294-4 | |
MD MD |
% | ASTM D955 | |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ASTM D570 | |
23℃,24hr 23℃,24hr |
% | ASTM D570 | |
23℃,24hr 23℃,24hr |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
ASTM D256 | ||
23℃ 23℃ |
kJ/m² | ISO 180-A | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
ISO 180 | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 6 |
|||
23℃,Total Energy 23℃,Total Energy 6 |
J | ASTM D3763 | |
拉伸冲击强度 Tensile impact strength |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 7 | |
B50 B50 |
℃ | ISO 306 | |
球压温度 Ball pressure temperature |
℃ | IEC 60335-1 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~82℃ MD:-40~82℃ |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
2.00 mm,解决方案 A 2.00 mm, solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 8 |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire 8 |
|||
2 mm,5.0 sec 2 mm,5.0 sec 8 |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index 8 |
% | ISO 4589-2 | |
平均燃烧程度 Average combustion degree |
cm | ASTM D635 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength |
|||
断裂 fracture 2 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield |
% | ISO 527-2/50 | |
屈服 yield 3 |
% | ASTM D638 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 4 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 |
MPa | ISO 178 | |
泰伯耐磨性 Taber abraser |
% | ASTM D1044 | |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 方法 I (三点负荷), 0.079 in/min |
4 0.079 in/min |
5 11.1 ft/sec |
6 速率 A (50°C/h), 载荷2 (50N) |
7 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
8 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
【新闻资讯】查看全部
聚焦碳达峰、碳中和 汽车行业加速电动化转型
2021-04-23 搜料网资讯: 12个室内展馆、36万平展出面积、1000家企业参展4月19日,第十九届上海国际汽车工业展览会如期举行。针对中国提出的2030年碳达峰、2060年碳中和的目标,全球汽车品牌中的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |