牌号简介 About |
---|
POM共聚物易流动注射成型型,适用于高刚性、高硬度、高韧性的精密成型件和薄壁成型件;耐溶剂、燃料、强碱性好,耐水解性好;耐高温氧化降解。根据21 CFR 177.2470燃烧率ISO 3795和厚度大于1 mm的fmvss 302<75 mm/min,根据VDA 275<10 mg/kg的单体和添加剂的排放列在符合欧盟法规(EU)10/2011的FDA中。应用范围:汽车工程,精密工程,电工电子工业,家用电器。FDA=食品药品监督管理局(美国)fmvss=联邦机动车辆安全标准(美国) POM copolymer Easy flowing Injection molding type for precision molded parts and thin-walled molded parts with high rigidity, hardness and toughness; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation. Emission according to VDA 275 < 10 mg/kg Monomers and additives are listed in EU-Regulation (EU) 10/2011 FDA compliant according to 21 CFR 177.2470 Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm. Ranges of applications: automotive engineering, precision engineering, electric and electronical industry, domestic appliances. FDA = Food and Drug Administration (USA) FMVSS = Federal Motor Vehicle Safety Standard (USA) |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
2900 | MPa | ISO 527-2/1A/1 |
拉伸强度 tensile strength |
|||
屈服 yield |
65.0 | MPa | ISO 527-2/1A/50 |
拉伸应变 Tensile strain |
|||
屈服 yield |
9.0 | % | ISO 527-2/1A/50 |
标称拉伸断裂应变 Nominal tensile fracture strain |
25 | % | ISO 527-2/1A/50 |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
2500 | MPa | ISO 899-1 |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体体积流动速率 Melt Volume Rate |
|||
190℃,2.16 kg 190℃,2.16 kg |
cm³/10min | ISO 1133 | |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
% | ISO 294-4 | |
MD MD |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
熔体密度 Melt density |
g/cm³ | ||
Melt Specific Heat Melt Specific Heat |
J/kg/℃ | ||
熔体导热性 Melt thermal conductivity |
W/m/K | ||
顶出温度 Ejection temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
【新闻资讯】查看全部
博禄最新处置方案亮相CHINAPLAS大舞台
2016-04-28 博禄在CHINAPLAS的展台展示其创新塑料解决方案,其专家更与观众一起交流塑料行业最新趋势。 此次,中国的家居用品生产商又将体验到博禄应用于家居用品的全新材料:具有出色透明度的无规共聚聚丙烯――RG568MO。这是首款利用博禄自行研发的无规共聚技术生产的聚丙烯材料,其制品外表更美观、内容物更清晰可见。 在基建领域,博禄的聚乙烯管道解决方案凭借卓越的耐用性和安全性受到中国基础设施产品供应商的一致肯定。在本届展会上,博禄推出了最新产品黄色PE80混配料BorS |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |