牌号简介 About |
---|
优异的抗环境应力、抗裂性、高冲击强度、良好的挤出特性,采用非食品级抗静电剂配制,符合:美国FDA 21 CFR 175.105有关详细信息,请参阅相关法规。UNIVAL™ DMDF-6230 NT高密度聚乙烯(HDPE)树脂专门设计用于间歇或连续吹塑设备中,以生产20加仑以下的容器,这些容器的尺寸要求结合卓越的环境应力抗裂性(ESCR)和高冲击强度。Univeal DMDF-6230 NT高密度聚乙烯树脂也被认为是一种多用途吹塑树脂,设计用于高速生产吹塑容器,用于包装家用工业化学品(如洗涤剂、漂白剂、织物柔软剂)、洗漱用品和化妆品(如洗发水、面霜、乳液等)、保健和医疗辅助用品。此外,它可以吹塑成其他薄壁零件和家庭用品,也可以挤压成型材或片材。 Outstanding environmental stress crack resistance High impact strength Good extrusion characteristics Formulated with a non-food grade antistatic agent Complies with: U.S. FDA 21 CFR 175.105 Consult the regulations for complete details. UNIVAL™ DMDF-6230 NT High Density Polyethylene (HDPE) Resin is specifically designed for use in either intermittent or continuous blow molding equipment to produce containers up to 20 gallons in size -applications that require the combination of outstanding environmental stress crack resistance (ESCR) and, high impact strength. UNIVAL DMDF- 6230 NT HDPE resin is also considered a multipurpose blow molding resin designed for the high speed production of blow molded containers used for packaging household industrial chemicals (e.g., detergents, bleach, fabric softeners), toiletries and cosmetics (e.g., shampoos, creams, lotions, etc.), health and medicinal aids. In addition, it can be blow molded into other thin walled parts and houseware items, and also can be extruded into profiles or sheets. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.949 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.25 | g/10min | |
190℃,21.6kg 190℃,21.6kg |
25 | g/10min | |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
50 ℃,100%非离子表面活性剂,F50 50 ℃, 100% non-ionic surfactant, F50 |
180 | hr | ASTM D1693 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸冲击强度 Tensile impact strength 2 |
210 | kJ/m² | ASTM D1822 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
结晶峰温度 Crystallization peak temperature |
|||
DSC DSC |
℃ | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
MPa | ||
断裂 fracture |
MPa | ||
拉伸应变 Tensile strain |
ASTM D638 | ||
屈服 yield |
% | ||
断裂 fracture |
% | ||
弯曲模量 Bending modulus |
|||
正割 Secant |
MPa | ASTM D790-B |
备注 |
---|
1 With limitations |
2 一般属性:这些不能被视为规格。 |
3 类型 S |
【新闻资讯】查看全部
第二十四届冬季奥林匹克运动会在京隆重开幕 习近平出席开幕式并宣布
2022-02-12 新华社北京2月4日电 筑梦冰雪,同向未来。2022年2月4日晚,举世瞩目的北京第二十四届冬季奥林匹克运动会开幕式在国家体育场隆重举行。国家主席习近平出席开幕式并宣布本届冬奥会 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |