| 牌号简介 About |
|---|
| Bormed™ HG820MO是一种用于医疗应用评估的树脂。Bormed™ HG820MO是一种具有内部润滑剂的澄清均聚物，通常用于注塑成型。从Bormed™ HG820MO生产的产品的特点是易于脱模，控制低摩擦和低翘曲。Bormed™ HG820MO可以用环氧乙烷或蒸汽灭菌。 Bormed HG820MO is a resin intended for evaluation for use in Healthcare applications. Bormed HG820MO is a clarified homopolymer and typically used in injection moulding. Additivation has been optimized to provide good demoulding properties. This polymer is a CR (controlled rheology) grade with narrow molecular weight distribution giving low risk of warpage. Bormed HG820MO can be sterilised with ethylene oxide or steam. Applications Bormed HG820MO has been evaluated according to different regulations and norms. Typical applications are mentioned below for Medical devices or Pharmaceutical & Diagnostic packaging. However, Borealis should be consulted for final approval to evaluate the use of Bormed HG820MO . Disposable non pre-filled syringes Laboratory disposable This grade may only be used for the applications listed in the Product Datasheet and only to the extent that the application is within the scope of the tests set out in the Statement on Compliance to Regulations on Medical Use for that grade. If an application is not listed in the Product Datasheet, the grade can be used for such application only after express written consent of the Borealis Marketing Manager, Healthcare. Borealis prohibits the use of any healthcare grade product in an implantable device that is introduced into the human body by surgical intervention and that is intended to remain in place following surgical procedure. Special Features Easy processing Good transparency |
产品描述 Product Description
用途：医疗/护理用品;药物;包装;
加工条件：注射成型 Injection Molding
性能特点： 可回收; 均聚物; 低翘曲性; 低摩擦系数; 易加工; Low warping,Excellent Processability,Renewable resources,Low coefficient of friction,Homopolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.905 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
28 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
50 mm 50 mm |
1900 | MPa | ISO 527-2 |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
40.0 | MPa | ISO 527-2/50 |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield |
7.0 | % | ISO 527-2/50 |
|
弯曲模量 Bending modulus 2 |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2.0 in/min |
|
【新闻资讯】查看全部 
软PVC管材的生产工艺及制品缺陷处理方法
2016-10-20 软PVC管材的生产流程分为：原料前处理、捏合、造粒、挤出管材4个部分： 1、原料前处理将所用的PVC树脂、增塑剂、稳定剂、润滑剂、填充剂、颜料等进行过筛、研磨。 2、捏合将处理好的原料用低效捏合机进行较长时间的捏合，使得各种配料分散均匀，膨润吸收效果良好。 3、造粒可采取挤出或压延混炼两种方法将捏合料造粒。 4、挤出管材用挤出机按其出料方式分为平挤垂拉法[见图(a)]和平挤平拉法[见图(b)]进行挤出管材。 |
|