牌号简介 About |
---|
MonoSol® AF A200是一种基于聚乙烯醇的热塑性薄膜,可溶于热水,使用Monosol AF的专有吹塑薄膜技术制造。MonoSol® AF A200是一种典型的聚乙烯醇热水溶性薄膜。在60℃以上,经搅拌可溶解。它具有有限的冷湿强度,主要用于医院洗衣袋,其中大部分亚麻布是干的。它也可用于某些化学部分包装应用的VFFS包装机械,其中包装被置于60°C以上的水和搅拌环境中。可用厚度范围为20微米(0.8密耳)至80微米(3.1密耳)。 MonoSol AF A200 is a PVOH based thermoplastic film, soluble in hot water and manufactured using MonoSol AF's proprietary blown film technology. MonoSol AF A200 is a typical grade of PVOH hot water-soluble film. It is soluble above 60°C with agitation. It has limited cold wet strength and is primarily used for hospital laundry bags where the bulk of the linen is dry. It can also be used on some VFFS machinery for delivery system applications where the film is being put into an environment with water above 60°C with agitation. Available thickness range is 20 micron (0.8 mil) to 80 micron (3.1 mil). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
含水量 water content 2 |
|||
23℃ 23℃ 2 |
6.7 | % | |
可溶性 solubility 3 |
|||
Disintegration:60℃,20.0 µm Disintegration:60℃,20.0 µm |
1.0 | sec | |
Disintegration:70℃,20.0 µm Disintegration:70℃,20.0 µm |
1.0 | sec | |
Dissolution:60℃,20.0 µm Dissolution:60℃,20.0 µm |
430.0 | sec | |
Dissolution:70℃,20.0 µm Dissolution:70℃,20.0 µm |
300.0 | sec | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
薄膜厚度 film thickness |
|||
割线模量 Secant modulus |
ASTM D882 , ISO 527-3 | ||
10%,MD:20 µm 10%,MD:20 µm |
MPa | ASTM D882 , ISO 527-3 | |
100%,MD:20 µm 100%,MD:20 µm |
MPa | ASTM D882 , ISO 527-3 | |
10%,TD:20 µm 10%,TD:20 µm |
MPa | ASTM D882 , ISO 527-3 | |
100%,TD:20 µm 100%,TD:20 µm |
MPa | ASTM D882 , ISO 527-3 | |
拉伸强度 tensile strength |
|||
MD,断裂,20 µm MD, fracture, 20 µ m |
MPa | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
MPa | ASTM D882 | |
MD,20 µm MD,20 µm |
MPa | ISO 527-3 | |
TD,20 µm TD,20 µm |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ASTM D882 , ISO 527-3 | ||
MD,断裂,20 µm MD, fracture, 20 µ m |
% | ASTM D882 , ISO 527-3 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
% | ASTM D882 , ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
20 µm 20 µm |
g | ASTM D1709,DIN 53433 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD:20 µm MD:20 µm |
g | ASTM D1922 | |
TD:20 µm TD:20 µm |
g | ASTM D1922 | |
MD:20 µm MD:20 µm |
N | ISO 6383-2 | |
TD:20 µm TD:20 µm |
N | ISO 6383-2 | |
用量 dosage |
|||
20.0 µm 20.0 µm |
m²/kg | ASTM D4321 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Distilled Water (MSTM 205) |
3 50%RH |
【新闻资讯】查看全部
2018年上海工业单位添加值能耗下降34.9%
2019-01-29 新版上海产业能效指南1月24日发布,这是上海制造业绿色发展的重要标尺,为其“以能耗论英雄”提供技术支撑。 数据显示,与2011年相比,2018年上海市规上工业单位增加值能耗累计下降了34.9%,单位能源消费的经济产出提升了53.6%。上海市乙烯、甲醇、MDI、醋酸等产品单耗处于国内先进水平。但是,上海市仍有部分指标处于国内一般水平,能效仍有提升空间。 上海市经信委方面称,2019年将从开展能效对标、探索智慧节能、创建绿色制造标杆、培育发展节能环保产业、推进节 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |