Sarlink TPV 5700B系列是高度工程化的挤出级热塑性硫化橡胶,具有出色的紫外线稳定性,适用于要求严格的汽车内外密封应用,包括玻璃槽、腰带、挡风雨条、密封件和其他型材。Sarlink® TPV X5735B是一种低硬度、低密度、高性能的产品,具有低雾化、优异的保色性和弹性。 The Sarlink TPV 5700B series are highly engineered extrusion-grade thermoplastic vulcanizates with outstanding UV stability designed for demanding automotive interior and exterior sealing applications, including glass run channels, waistbelts, weather strips, seals and other profiles. Sarlink TPV X5735B is a low hardness, low density, high performance grade with low fogging and excellent color retention and elastic properties. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.928 | g/cm³ | ASTM D792 |
密度 Density |
0.930 | g/cm³ | ISO 1183 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
TD,100% 应变 TD, 100% strain |
0.800 | MPa | ASTM D412 |
MD,100% 应变 MD, 100% strain |
1.70 | MPa | ASTM D412 |
拉伸强度 tensile strength |
ISO 37 | ||
TD,100% 应变 TD, 100% strain |
0.800 | MPa | ISO 37 |
MD,100% 应变 MD, 100% strain |
MPa | ISO 37 | |
拉伸强度 tensile strength |
ASTM D412 | ||
断裂 fracture |
MPa | ASTM D412 | |
MD,断裂 MD, fracture |
MPa | ASTM D412 | |
拉伸强度 tensile strength |
ISO 37 | ||
断裂 fracture |
MPa | ISO 37 | |
MD,断裂 MD, fracture |
MPa | ISO 37 | |
拉伸应变 Tensile strain |
ASTM D412 | ||
断裂 fracture |
% | ASTM D412 | |
流量,断裂 Flow rate, fracture |
% | ASTM D412 | |
拉伸应变 Tensile strain |
ISO 37 | ||
断裂 fracture |
% | ISO 37 | |
流量,断裂 Flow rate, fracture |
% | ISO 37 | |
撕裂强度 tear strength 2 |
|||
TD TD |
kN/m | ASTM D624 | |
TD TD 2 |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
ASTM D395 | ||
23℃,22 hr 23℃,22 hr |
% | ASTM D395 | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395 | |
125℃,70 hr 125℃,70 hr |
% | ASTM D395 | |
压缩形变 Compression deformation |
ISO 815 | ||
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A,5 秒,挤出成型 Shore A, 5 seconds, extrusion molding |
ISO 868 | ||
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
ISO 868 | ||
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,5 秒,挤出成型 Shore A, 5 seconds, extrusion molding |
ASTM D2240 | ||
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
ASTM D2240 | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 - TD Change rate of tensile strength in air - TD |
ASTM D573 | ||
135℃,1000 hr 135℃,1000 hr |
% | ASTM D573 | |
100% 应变,135℃,1000 hr 100% strain, 135 ℃, 1000 hr |
% | ASTM D573 | |
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
100% 应变,150℃,168 hr 100% strain, 150 ℃, 168 hr |
% | ASTM D573 | |
空气中拉伸强度的变化率 - TD Change rate of tensile strength in air - TD |
ISO 188 | ||
135℃,1000 hr 135℃,1000 hr |
% | ISO 188 | |
100% 应变 135℃,1000 hr 100% strain 135 ℃, 1000 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
100% 应变 150℃,168 hr 100% strain 150 ℃, 168 hr |
% | ISO 188 | |
空气中极限伸长率的变化率 - TD Change rate of ultimate elongation in air - TD |
ASTM D573 | ||
135℃,1000 hr 135℃,1000 hr |
% | ASTM D573 | |
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
在空气中断裂时拉伸应力变化 - TD Changes in tensile stress when fractured in air - TD |
ISO 188 | ||
135℃,1000 hr 135℃,1000 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
ASTM D573 | ||
邵氏 A,135℃,1000 hr Shaw A, 135 ℃, 1000 hr |
ASTM D573 | ||
邵氏 A,150℃,168 hr Shaw A, 150 ℃, 168 hr |
ASTM D573 | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
ISO 188 | ||
邵氏 A,135℃,1000 hr Shaw A, 135 ℃, 1000 hr |
ISO 188 | ||
邵氏 A,150℃,168 hr Shaw A, 150 ℃, 168 hr |
ISO 188 | ||
体积变化 Volume change |
|||
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ISO 1817 | |
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体表观粘度 - Capillary @ 206/s Apparent viscosity of melt - Capillary @ 206/s |
|||
200℃ 200℃ |
Pa·s | ISO 11443 | |
200℃ 200℃ |
Pa·s | ASTM D3835 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 B 方法,直角形试样(不割口) |
【新闻资讯】查看全部
攻关智能化 金明精机将设智能配备研讨院
2016-02-25 据金明精机最新公告,为适应未来业务发展的需要,强化公司智能制造能力,提升产品智能化水平,拟在广东汕头以自有资金投资设立全资子公司汕头市金明智能装备研究院有限公司(暂名,以工商行政管理部门注册登记为准)。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |