Valox Enh4550树脂,25%玻璃纤维增强,无溴无氯阻燃剂,PBT树脂。 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 3 |
9900 | MPa | ASTM D638 |
拉伸模量 Tensile modulus |
10400 | MPa | ISO 527-1-2 |
拉伸强度 tensile strength |
|||
断裂 fracture |
112 | MPa | ISO 527-2/5 |
断裂 fracture 4 |
105 | MPa | ASTM D638 |
屈服 yield 4 |
105 | MPa | ASTM D638 |
屈服 yield |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
屈服 yield 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 6 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
弯曲强度 bending strength 6 , 7 |
MPa | ISO 178 | |
弯曲强度 bending strength 5 |
|||
屈服,50 mm跨度 Yield, 50 mm span 5 |
MPa | ASTM D790 | |
断裂弯曲应变 Fracture bending strain 8 |
% | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ISO 179/2C | |
23℃ 23℃ 9 |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/2C | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/2U | ||
-30℃ -30℃ |
kJ/m² | ISO 179/2U | |
23℃ 23℃ |
kJ/m² | ISO 179/2U | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 10 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D4812 | ||
-30℃ -30℃ |
J/m | ASTM D4812 | |
23℃ 23℃ |
J/m | ASTM D4812 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 10 |
ISO 180/1U | ||
-30℃ -30℃ |
kJ/m² | ISO 180/1U | |
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 11 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 11 |
℃ | ISO 75-2/Bf | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 12 | |
-- -- |
℃ | ASTM D1525 13 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
ASTM D149 | ||
3.2 mm,在空气中 3.2 mm in air |
kV/mm | ASTM D149 | |
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
耐电弧性 Arc resistance 14 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.8 mm 0.8 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm 15 |
℃ | IEC 60695-2-13 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
密度 Density |
g/cm³ | ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,5.0kg 250℃,5.0kg |
g/10min | ASTM D1238 | |
熔体体积流动速率 Melt Volume Rate |
|||
250℃,5 kg 250℃,5 kg |
cm³/10min | ISO 1133 | |
收缩率 Shrinkage rate |
Internal Method | ||
TD TD 2 |
% | 内部方法 | |
TD:3.2 mm TD:3.2 mm |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
熔体表观粘度 Apparent viscosity of melt |
|||
250℃,1500 sec^-1 250℃,1500 sec^-1 |
Pa·s | ISO 11443 | |
特殊值 Special value |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Tensile Bar |
3 0.20 in/min |
4 类型 1, 0.20 in/min |
5 0.051 in/min |
6 0.079 in/min |
7 Yield |
8 Break |
9 2 mm/min |
10 80*10*4 sp=62mm |
11 80*10*4 |
12 80*10*4 mm |
13 标准 B (120°C/h), 载荷2 (50N) |
14 速率 A (50°C/h), 载荷2 (50N) |
15 钨电极 |
16 by VDE |
【新闻资讯】查看全部
罗姆PMMA为音乐播放器打造变色板光效,显示屏与外壳融为一体
2020-12-25 搜料网资讯: 在音乐数字化时代,播放器的需求并未消失事实上,唱片机+Hi-Fi系统衍生而来的数字网络播放器,凭借高品质设计和智能化弥补了唱片机时代的仪式感:小心翼翼将唱片放 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |