牌号简介 About |
---|
伊娃树脂AlCudia PA-420L具有低凝胶含量,推荐用于挤出涂布应用,尤其是当需要高生产速度时。PA-420-L还特别适用于与其他聚合物共挤出。它含有抗氧化剂和自由流动剂。典型应用:层压(如图形艺术)共挤包装膜PA-420-L中的挤出涂层热粘合层设计用于在高达220°C的高温下在高速挤出涂层生产线中加工。各生产线的加工条件应得到优化。 EVA resin ALCUDIA® PA-420-L features low gel content and is recommended for extrusion coating applications, especially when high productions speeds are required. PA-420-L is also particularly suitable for co-extrusion with other polymers. It contains antioxidant and free flowing agent. TYPICAL APPLICATIONS Extrusion coating Thermal adhesive layer in lamination (e.g. graphic arts) Co-extrusion Packaging films PA-420-L is designed to be processed at temperatures as high as 220°C in high speed extrusion coating lines. Processing conditions should be optimised for each production line. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.940 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
20 | g/10min | ISO 1133 |
醋酸乙烯含量 Vinyl acetate content |
20.0 | wt% | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
53.0 | ℃ | ISO 306/A |
熔融温度 Melting temperature |
82.0 | ℃ | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
|||
邵氏 D Shaw's D |
|||
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
帝斯曼(美国)埃文斯维尔工厂生产规模扩大
2021-03-28 搜料网资讯: 帝斯曼(美国)工程塑料公司(简称DSM EPA)计划扩大印第安纳州埃文斯维尔的生产规模,截至今年底,将创造25个新岗位。 帝斯曼EPA 在埃文斯维尔占地175,000平方英尺的化学工厂 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |