| 牌号简介 About |
|---|
| P-125是一种半透明、高撕裂强度、铂催化的RTV-2硅橡胶，设计用于需要目视检查的铸造零件。它很容易混合和脱气，并将治愈几乎没有收缩。橡胶硬化的速度可以通过加热或室温下的铂加速器显著加快。加成固化双组分硅橡胶具有优异的耐化学性和耐热性，但可能表现出一定的抑制敏感性。P-125非常适用于需要优良机械性能的原型应用。 P-125 is a translucent, high tear strength, platinum-catalyzed, RTV-2 silicone rubber, which was designed for casting parts where visual inspection is required. It is easy to mix and de-air, and will cure with virtually no shrinkage. The speed at which the rubber hardens can be dramatically accelerated with heat or with Pt Accelerator at room temperature. Addition-cure two-component silicone rubbers exhibit excellent chemical and heat resistance, but may show some inhibition sensitivity. P-125 is extremely useful for prototype applications where superior mechanical properties are required. |
产品描述 Product Description
性能特点： 耐化学性; 耐高温; High Heat Resistance,Solvent resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.09 | g/cm³ | |
|
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
颜色 colour |
|||
|
-- -- 3 |
Clear/Transparent | ||
|
-- -- 4 |
Translucent | ||
|
粘度 viscosity |
|||
|
-- -- 3 |
1.0 到 2.0 | Pa·s | |
|
-- -- 4 |
160 到 180 | Pa·s | |
|
固化时间 Curing time |
hr | ||
|
储存稳定性 storage stability |
min | ||
|
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 A Shaw's A 6 |
|||
|
拉伸强度 tensile strength |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D412 | |
|
撕裂强度 tear strength |
kN/m | ASTM D624 | |
|
耐电强度 Electrical strength |
kV/mm | ||
|
相对电容率 Relative permittivity |
|||
|
100 Hz 100 Hz |
|||
|
体积电阻率 Volume resistivity |
ohms·cm | ||
|
耗散因数 Dissipation factor |
|||
|
100 Hz 100 Hz |
|||
|
Coverage（Cured） Coverage（Cured） |
cm³/g | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
使用温度 Operating temperature |
|||
|
Cured Cured |
℃ | ||
|
热固组件 Thermosetting components |
|||
|
树脂 resin |
|||
|
硬化法 Hardening method |
|||
|
贮藏期限 Storage period |
wk | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Mixed |
| 3 Activator |
| 4 Base |
| 5 7 Days |
| 6 1 Day |
|
【新闻资讯】查看全部 
塑料物理测试
2017-06-21 塑料物理测试 多面体实验室根据ASTM标准进行塑性物理测试。多面体还提供额外的物理测试，例如气体膨胀比重瓶的密度。 多面体进行的一些ASTM标准塑料物理测试包括：在高温(2小时 |
|