牌号简介 About |
---|
Durethan®BKV215 H3.0 000000(干燥)PA 6-共聚物,15%玻璃纤维,注塑成型,改善冲击强度,热老化稳定 Durethan®BKV215 H3.0 000000 PA 6-共聚物,15%玻璃纤维,注塑 成型,提高冲击强度,热老化稳定 Durethan® BKV215H3.0 000000 (Dry) PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized Durethan® BKV215H3.0 000000 PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized Durethan® BKV215H3.0 000000 PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.18 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.60 | g/cm³ | ISO 60 |
收缩率 Shrinkage rate |
ISO 2577 | ||
TD:280℃,3.0 mm TD:280℃,3.0 mm |
0.83 | % | ISO 2577 |
TD:120℃,3.0 mm,4 hrs TD:120℃,3.0 mm,4 hrs |
0.15 | % | ISO 2577 |
MD:280℃,3.0 mm MD:280℃,3.0 mm |
0.30 | % | ISO 2577 |
MD:120℃,3.0 mm,4 hrs MD:120℃,3.0 mm,4 hrs |
% | ISO 2577 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178-A | |
弯曲强度 bending strength |
ISO 178/A | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ISO 178-A | |
23℃ 23℃ |
MPa | ISO 178-A | |
弯曲应变 Bending strain |
% | ISO 178/A | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180/1U | ||
-30℃ -30℃ |
kJ/m² | ISO 180/1U | |
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B120 B120 |
℃ | ISO 306/B120 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
ISO 1874 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 150x105x3mm, 80°C MT, 400 bar |
3 150x105x3mm |
4 0.079 in/min |
5 2 mm/min |
6 10°C/min |
7 程序 A |
【新闻资讯】查看全部
大规模定制鞋品、眼镜及牙科应用将迎爆发性增长
2021-04-18 搜料网资讯: 惠普(HP)近日发布了2020年3D打印及数字制造趋势。通过对一组专家的采访,惠普确认了将对推动工业4.0有重大影响的主要趋势,包括对可持续生产的需求、自动化如何改变工 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |