牌号简介 About |
---|
聚酯玻璃纤维增强35%,耐高温,耐化学性很好,力学、热学、电学性能很好,吸水率很低,尺寸稳定性很好。产品成型前必须干燥。可供选择:所有颜色,热稳定(H),释放剂(W)。 PET glass fiber reinforced 35%, very high temperature resistance, very good chemical resistance, very good mechanical, thermal and electrical properties, very low moisture absorption, very good dimensional stability. Product must be dryed before moulding. Available: all colors, heat stabilized (H), release agent (W). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.62 到 1.64 | g/cm³ | ASTM D792 , ISO 1183 |
收缩率 Shrinkage rate |
ASTM D955 | ||
MD MD |
0.15 到 0.30 | % | ASTM D955 |
TD TD |
0.40 到 0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.050 | % | ASTM D570,ISO 62 |
Granule Humidity Granule Humidity |
< 0.030 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 , ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 , ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 , ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 , ISO 178 | |
弯曲强度 bending strength |
|||
-- -- |
MPa | ISO 178 | |
断裂 fracture |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 2 |
|||
23℃ 23℃ 2 |
kJ/m² | ASTM D256,ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 2 |
|||
23℃ 23℃ 2 |
kJ/m² | ASTM D256,ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256,ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648,ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306/B50 , ASTM D1525 3 | |
球压测试 Ball pressure test |
|||
245℃ 245℃ |
USI 182-2 | ||
熔融温度 Melting temperature |
℃ | ASTM D211,ISO 121 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-30~30℃ MD:-30~30℃ |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
1 mm 1 mm |
kV/mm | ASTM D149 | |
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.00 mm 1.00 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 6x4x50 mm |
3 速率 A (50°C/h), 载荷2 (50N) |