钻石HI-860和HI-861是高冲击聚苯乙烯,具有良好的光泽和抗应力开裂(制冷级)。Hi-860是一种设计用于注塑成型的易流动材料,Hi-861也是一种设计用于挤出成型的易流动抗氟利昂材料。 Diamond HI-860 is a High Impact Polystyrene grade with Opaque & matt finish surface. It gives excellent mechanical and heat resistance properties while providing with easy process ability and molding applications. Characteristics: High impact, Standard flow Good gloss, Low volatility Stress cracking. Applications: Molded parts of Freezers and Deep freezers. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
1.05 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
5.0 | g/10min | ASTM D1238 |
吸水率 Water absorption rate |
|||
23℃,24hr,50% RH 23℃,24hr,50% RH |
< 0.10 | % | |
平衡 balance |
< 0.10 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
16.7 | MPa | ASTM D638 |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
J/m | ASTM D256 | |
落锤冲击 Drop hammer impact |
J | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
沙特阿美转让4%股份予PIF将推动可再生能源发展
2022-02-19 沙特公共投资基金(PIF)是沙特可再生能源的最大投资者之一 PIF得到沙特政府授权将70%的资产投资于清洁能源 沙特阿美将不会从4%股份转让中获取任何收益 中化新网讯 据电力/能源转型 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |