牌号简介 About |
---|
Ryton® R-7-150BL玻璃纤维和矿物填充聚苯硫醚化合物在持续或反复暴露于高温水中后提供增强的机械强度。 Ryton® R-7-150BL glass fiber and mineral filled polyphenylene sulfide compound provides enhanced mechanical strength after constant or repeated exposure to high temperature water. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
1.95 | g/cm³ | ISO 1183 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.020 | % | ASTM D570 |
收缩率 Shrinkage rate 3 |
|||
MD MD |
0.20 | % | |
TD TD |
0.40 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
165 | MPa | ISO 527 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180/A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-50~50℃ MD:-50~50℃ |
1/℃ | ||
MD:100~200℃ MD:100~200℃ |
1/℃ | ||
TD:-50~50℃ TD:-50~50℃ |
1/℃ | ||
TD:100~200℃ TD:100~200℃ |
1/℃ | ||
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1530 | |
热变形温度 Hot deformation temperature |
|||
1.8 MPa 1.8 MPa |
℃ | ASTM D648 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
25 ℃,1 kHz 25 ℃,1 kHz |
|||
25 ℃,1 MHz 25 ℃,1 MHz |
|||
耗散因数 Dissipation factor |
|||
25℃,1 kHz 25℃,1 kHz |
|||
25℃,1 MHz 25℃,1 MHz |
|||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index 4 |
V | UL 746 | |
绝缘电阻 insulation resistance |
|||
95% RH,48 hr,90℃ 95% RH,48 hr,90℃ |
ohms | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm 4 |
UL 94 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
水解稳定性 Hydrolysis stability 5 |
|||
拉伸强度 Retained Tensile strength Retained |
% | ||
体重增量 Weight gain |
% | ||
|
备注 |
---|
2、方法 A |
3、Measured on 102 mm x 102 mm x 3.2 mm plaques, edge gated. |
4、This product is not currently UL listed; test results indicate this level of performance. |
5、Test specimens aged 1000 hours in water at 140°C (284°F). |
【新闻资讯】查看全部
伊朗官员称燃油价格下跌对通胀的影响被过分夸张
2018-01-09 伊朗《金融论坛报》1月4日报道,3日伊朗财经部副部长米尔索贾万(Hossein Mirshojaiyan)表示,一些经济学家担心燃油价格上涨计划会把通货膨胀率推高8%,这种预测很可能被过分夸大。他表示,燃油价格上涨50%,即汽油提价至1.5万里亚尔/升(34.8美分)、柴油提价至0.4万里亚尔/升(9.3美分),最多会把通货膨胀率推高1.5%;伊朗计划与预算组织、伊朗央行的预测为2%。 伊朗议会经济委员会主席波伊布拉希米(Mohammad Reza Pour-Ebrahim |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |