| 牌号简介 About |
|---|
| MonoSol® AF L337是一种基于聚乙烯醇的热塑性薄膜，可溶于冷水，使用Monosol AF的专有吹塑薄膜技术制造。MonoSol® AF L337是一种高度塑化级的聚乙烯醇冷水溶性包装膜，具有良好的膜-膜粘结性，是拉伸包装应用的膜选择。可用厚度范围为20微米（0.8密耳）至60微米（2.4密耳）。 MonoSol AF L337 is a PVOH based thermoplastic film, soluble in cold water and manufactured using MonoSol AF's proprietary blown film technology. MonoSol AF L337 is a highly plasticized cold water-soluble film with good solubility, toughness and cold crack resistance. In bag form, MonoDose™ L337 film is a leading candidate for powder delivery systems with no special requirements or contraindications. It can also be used for special applications such as self adhesive labels, lamination, and soluble dams for inert gas welding of SS pipe. Available thickness range is 20 micron (0.8 mil) to 60 micron (2.4 mil). |
产品描述 Product Description
用途：薄膜;拉伸缠绕;
性能特点： 经增塑; 水溶性; 生物可降解; Biodegradable,Water soluble,Plasticizing
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
含水量 water content 2 |
|||
|
23℃ 23℃ 2 |
7.6 | % | |
|
可溶性 solubility 3 |
|||
|
Disintegration：10℃，50.0 µm Disintegration：10℃，50.0 µm |
24.0 | sec | |
|
Disintegration：24℃，50.0 µm Disintegration：24℃，50.0 µm |
12.0 | sec | |
|
Dissolution：10℃，50.0 µm Dissolution：10℃，50.0 µm |
83.0 | sec | |
|
Dissolution：24℃，50.0 µm Dissolution：24℃，50.0 µm |
58.0 | sec | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
µm | ||
|
薄膜厚度 film thickness |
|||
|
割线模量 Secant modulus |
ASTM D882 , ISO 527-3 | ||
|
10%，MD：50 µm 10%，MD：50 µm |
MPa | ASTM D882 , ISO 527-3 | |
|
100%，MD：50 µm 100%，MD：50 µm |
MPa | ASTM D882 , ISO 527-3 | |
|
10%，TD：50 µm 10%，TD：50 µm |
MPa | ASTM D882 , ISO 527-3 | |
|
100%，TD：50 µm 100%，TD：50 µm |
MPa | ASTM D882 , ISO 527-3 | |
|
拉伸强度 tensile strength |
|||
|
MD，断裂，50 µm MD, fracture, 50 µ m |
MPa | ASTM D882 | |
|
TD，断裂，50 µm TD, fracture, 50 µ m |
MPa | ASTM D882 | |
|
MD，50 µm MD，50 µm |
MPa | ISO 527-3 | |
|
TD，50 µm TD，50 µm |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
|||
|
MD，断裂，50 µm MD, fracture, 50 µ m |
% | ASTM D882 , ISO 527-3 | |
|
TD，断裂，5.0E-3 µm TD, fracture, 5.0E-3 µ m |
% | ASTM D882 | |
|
TD，断裂，50 µm TD, fracture, 50 µ m |
% | ISO 527-3 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
|
MD：50 µm MD：50 µm |
g | ASTM D1922 | |
|
TD：50 µm TD：50 µm |
g | ASTM D1922 | |
|
MD：50 µm MD：50 µm |
N | ISO 6383-2 | |
|
TD：50 µm TD：50 µm |
N | ISO 6383-2 | |
|
用量 dosage |
|||
|
50.0 µm 50.0 µm |
m²/kg | ASTM D4321 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 50%RH |
| 3 Distilled Water (MSTM 205) |
|
【新闻资讯】查看全部 
岳阳石化布局1500万吨炼油150万吨乙烯一体化项目
2021-05-08 搜料网资讯： 5月6日上午，岳阳市人大常委会党组书记、常务副主任向伟雄主持召开岳阳地区炼化一体化项目选址调度会会议。副市长李美云和相关部门负责人参加。 向伟雄指出，中石 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付