牌号简介 About |
---|
Trademark PE mLLD1918C是一种茂金属线性低密度聚乙烯产品,。 它可以通过共挤出成型进行加工,在北美洲有供货。 Trademark PE mLLD1918C的应用领域包括包装、电影、密封应用 和 食品接触应用。 特性包括: Antiblock 软件 高光泽度 高强度 可接触食品 良好的密封性能 Trademark PE mLLD1918C is a Metallocene Linear Low Density Polyethylene product. It can be processed by coextrusion and is available in North America. Applications of Trademark PE mLLD1918C include film, food contact applications, packaging and sealing applications. Characteristics include: Antiblock Food Contact Acceptable Good Sealability High Gloss High Strength |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
0.918 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
膜刺穿力 Membrane puncture force |
|||
25 µm 25 µm |
77.0 | N | ASTM D3763 |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:25 µm,吹塑薄膜 1% secant, MD: 25 µ m, blow molded film |
172 | MPa | ASTM D882 |
1% 正割,TD:25 µm,吹塑薄膜 1% secant, TD: 25 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:25 µm,吹塑薄膜 MD: 25 µ m, blow molded film |
g | ASTM D1922 | |
TD:25 µm,吹塑薄膜 TD: 25 µ m, blow molded film |
g | ASTM D1922 | |
始封温度 Initial sealing temperature |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
℃ | ASTM D3763 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25.4 µm,吹塑薄膜 45 °, 25.4 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze 2 |
|||
25.4 µm,吹塑薄膜 25.4 µ m, blow molded film 2 |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Base polymer only |
【新闻资讯】查看全部
地方两会聚焦石化业绿色低碳发展
2022-02-09 在前不久各地陆续召开的两会上,石油和化工行业绿色低碳发展成为两会代表委员关注的热点。推动磷石膏综合利用、探索炼油转型炼化一体发展新路径、谋划煤炭高效清洁利用等一批 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |