牌号简介 About |
---|
VYPET VNT 340 HD是一种40%玻璃/矿物增强聚酯注塑化合物,专为电气和结构应用而设计,具有高介电强度特点:高温性能、优异的强度和高刚度、优异的尺寸稳定性应用:电机支架连接器 Vypet VNT 340 HD is a 40% glass/mineral reinforced PET injection molding compound designed for electrical and structural applications, with High Dielectric Strength Features: High temperature performance Excellent strength & high stiffness Excellent dimensional stability Applications: Electric motors Brackets Connectors |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.64 | g/cm³ | ISO 1183 |
收缩率 Shrinkage |
ASTM D955 | ||
MD:2.0 mm MD:2.0 mm 2 |
0.25 | % | ASTM D955 |
MD:3.2 mm MD:3.2 mm 3 |
0.32 | % | ASTM D955 |
TD:2.0 mm TD:2.0 mm 2 |
0.53 | % | ASTM D955 |
TD:3.2 mm TD:3.2 mm 3 |
0.79 | % | ASTM D955 |
吸水率 Water Absorption |
|||
23℃,24hr 23℃,24hr |
% | ASTM D570 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 HDT |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Coeff.of linear therm expansion |
ISO 11359-2 | ||
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength 6 |
ASTM D149 | ||
23 ℃,1.6 mm,在油中 23 ℃, 1.6 mm, in oil |
kV/mm | ASTM D149 | |
23 ℃,3.2 mm,在油中 23 ℃, 3.2 mm, in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1 kHz 1 kHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 kHz 1 kHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating |
|||
0.75 mm 0.75 mm |
UL 94 | ||
燃烧速率 Burning Speed |
|||
1 mm 1 mm |
mm/min | ISO 3795 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
弯曲模量 Flexural Modulus 4 |
MPa | ISO 178 | |
弯曲强度 Flexural Strength 4 |
MPa | ISO 178 | |
压缩强度 compressive strength 5 |
MPa | ASTM D695 | |
剪切强度 shear strength |
MPa | ASTM D732 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 (2mmx60mmx60mm) |
3 (3.2mmx7.6mmx12.6mm) |
4 0.079 in/min |
5 0.051 in/min |
6 500 V/sec |
【新闻资讯】查看全部
两性型高分子聚丙烯酰胺满足水质要求
2017-06-30 随着经济建设的快速发展,水污染呈发展趋势,工业发达地区水域污染尤为严重水,资源短缺问题也日益突出,城市缺水现象越来越严重。在我国,农村地区的饮用水问题更为严重。农村地区饮用水的水源呈现分散、多样性和不稳定的特点,水源得不到有效保护,饮水处理往往只经简单的沉淀或澄清处理,不能有效杀灭细菌、病毒等微生物,更不能去除有机农药的残留物,使生活在农村地区的人群的生命健康受到严重影响。 两性型高分子聚丙烯酰胺是由丙烯酰胺(AM)单体经自由基引发聚合而成的水溶性线性高分子聚合物,具有良好 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |