| 牌号简介 About |
|---|
| MALAT 37W300是一种30%玻璃珠增强聚对苯二甲酸丁二醇酯，用于注塑成型。该产品有Natuel和Black（MALAT 37W300黑色8229）两种颜色可供选择，但也可根据要求提供其他颜色。它们结合了高机械、热和电气性能以及优异的耐化学性和尺寸稳定性应用MALAT 37W300旨在用于电气部件的注塑成型和汽车应用。包括内部、外部和电气和机械系统，例如：电器部件开关和连接器外壳仪表板部件门把手和支柱装饰件 MALAT 37W300 is a 30 % glass bead reinforced polybutylene terephthalate, intended for injection moulding. The product is available in natuel and black (MALAT 37W300 BLACK 8229) but other colours can be provided on request They combine high mechanical, thermal and electrical properties with excellent chemical resistance and dimensional stability APPLICATIONS MALAT 37W300 is intended for the injection moulding of electrical components and automotive applications including interior, exterior and electrical and mechanical systems, such as: Electrical appliance components Switches and connector housings Dashboard components Door handles and pillar trim |
产品描述 Product Description
用途：家电部件;电器外壳;电气元件;汽车外部零件;汽车电子;把手;汽车内部零件;
颜色：黑色,可用颜色,自然色
加工条件：注射成型 Injection Molding
性能特点： 可回收; 防火阻燃等级HB; 尺寸稳定性好; 耐化学性; 电气性好; Good Dimensional Stability,Good Electrical Properties,Renewable resources,Solvent resistance,HB
填料：玻璃珠 30
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.53 | g/cm³ | ISO 1183 |
|
收缩率 Shrinkage rate |
0.80 到 1.5 | % | |
|
吸水率 Water absorption rate |
|||
|
23℃，24hr 23℃，24hr |
0.060 | % | ISO 62 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
4100 | MPa | ISO 527-2 |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
51.0 | MPa | ISO 527-2 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
弯曲强度 bending strength 2 |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | ISO 3146 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
|||
|
2 mm 2 mm |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
100 Hz 100 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
100 Hz 100 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 at Break |
|
【新闻资讯】查看全部
江苏省消协曝光不合格儿童塑料饮水杯
2016-06-01 随着六一儿童节的来临,江苏省消协于近期对南京市场和网络平台销售的儿童塑料饮水杯进行了比较试验。在市售实体店和网络电商平台随机购买的37个品牌的 50个样品中,聚丙烯(PP)25个,达标率100%;聚碳酸酯(PC)22个,达标率95.5%; 丙烯腈-苯乙烯共聚物(AS)2个,达标率为0;聚苯乙烯(PS)1个,达标100%。 “从本次检测结果发现,不达标样品属于中低档价位。在选购这类产品时,应更关注商品的安全性能,不能只考虑价格因素。”省消协监督部赵鑫建议,消费者应进正规商店、 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付