TEKAPPO™ J910是一种聚苯醚 + PS (PPE+PS)产品,含有的填充物为10% 玻璃纤维增强材料。 它,在亚太地区有供货。 主要特性为:阻燃/额定火焰。 Features J910 is GF 10% reinforced PPO + HIPS. Application Electrical & Electronic Drying Product is dried and packed with a moisture content of <0.16%. Should the Packaging become damaged or be left open too long, then the material must be Dried. A too high moisture content can lead to a reduction of optical and Mechanical properties. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.14 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.20 到 0.50 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.060 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
73.5 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
5.0 | % | ASTM D638 |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 3 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 60°C Mold Temperature |
【新闻资讯】查看全部
科思创为浇注型聚氨酯弹性体推出全新产品
2018-05-31 浇注型聚氨酯弹性体的加工过程中可能会应用到芳香胺,如MOCA。作为广泛使用的TDI基预聚物的扩链剂,MOCA在预聚物机械性能方面增加了很多优势。然而,虽然易于处理, REACH(化学品的注册、评估、授权和限制)法规可能会在不久的将来对其进行各种约束。 预测未来MOCA可能被约束,第一个想法是用另一种胺扩链剂来代替它。然而,这种替换通常会对处理条件和/或性能造成相当不利的影响。 另一方面, MDI基预聚物可以提供一种有利的出路。这体系允许针对特定的性能。然而, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |