| 牌号简介 About |
|---|
| cycoloy c2800树脂无氯化和无溴阻燃PC+abs为各种应用提供平衡流动和冲击性能。cycoloy c2800树脂无氯化和无溴阻燃PC/abs为各种应用提供平衡流动和冲击。 CYCOLOY C2800 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a standard grade that can be injection molded. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 & 5VB flame rating. CYCOLOY C2800 resin is an excellent candidate for a wide variety of applications including business equipment, monitors, and enclosures. |
产品描述 Product Description
加工条件：注射成型 Injection Molding
性能特点： 无卤; 防火阻燃等级V-0; 防火阻燃等级V-2; 防火阻燃等级5VB; 阻燃; 冲击性能好; 易流动; High impact resistance,Good liquidity,Halogen free,Flame Characteristics,V-2,V-0,5VB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
ASTM D792 | ||
|
-- -- |
1.17 | g/cm³ | |
|
-- -- 1 |
1.18 | g/cm³ | |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
260℃，2.16kg 260℃，2.16kg |
16 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
内部方法 | ||
|
MD：3.2 mm MD：3.2 mm |
0.40 到 0.60 | % | |
|
TD：3.2 mm TD：3.2 mm |
0.40 到 0.60 | % | |
|
吸水率 Water absorption rate |
ASTM D570 | ||
|
24hr 24hr |
% | ||
|
平衡，23℃ Equilibrium, 23 ℃ |
% | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
23℃，Total Energy 23℃，Total Energy |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
ASTM D648 | ||
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ||
|
1.8 MPa，未退火，6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ||
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 7 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM E831 | ||
|
MD：-40~60℃ MD：-40~60℃ |
1/℃ | ||
|
TD：-40~60℃ TD：-40~60℃ |
1/℃ | ||
|
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
|
相对温度指数 Relative temperature index |
℃ | UL 746 | |
|
电气性能 Electrical performance |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
|||
|
3.2 mm，在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
50 Hz 50 Hz |
|||
|
60 Hz 60 Hz |
|||
|
100 Hz 100 Hz |
|||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
50 Hz 50 Hz |
|||
|
60 Hz 60 Hz |
|||
|
耐电弧性 Arc resistance 8 |
ASTM D495 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
|
高电弧燃烧指数（HAI） High Arc Burning Index (HAI) |
UL 746 | ||
|
高电压电弧起痕速率 High voltage arc marking rate |
|||
|
HVTR HVTR |
UL 746 | ||
|
热丝引燃 Hot wire ignition |
|||
|
HWI HWI |
UL 746 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
0.89 mm 0.89 mm |
|||
|
1.47 mm 1.47 mm |
|||
|
2.31 mm 2.31 mm |
|||
|
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength 3 |
|||
|
屈服 yield 3 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain 4 |
ASTM D638 | ||
|
屈服 yield |
% | ||
|
断裂 fracture |
% | ||
|
弯曲模量 Bending modulus 5 |
|||
|
100 mm跨距 100 mm span 5 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 6 |
|||
|
屈服，100 mm跨度 Yield, 100 mm span 6 |
MPa | ASTM D790 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Color |
| 3 Tensile Bar |
| 4 2.0 in/min |
| 5 类型 1, 2.0 in/min |
| 6 0.10 in/min |
| 7 0.079 in/min |
| 8 Yield |
| 9 80*10*4 sp=62mm |
| 10 80*10*4 |
| 11 120*10*4 mm |
| 12 标准 B (120°C/h), 载荷2 (50N) |
| 13 Approximate maximum |
| 14 钨电极 |
|
【新闻资讯】查看全部
木塑产品蓬勃衰亡 终究优点何在？
2017-09-27 木塑，即木塑复合材料，是国内外近年蓬勃兴起的一类新型复合材料，指利用聚乙烯、聚丙烯和聚氯乙烯等，代替通常的树脂胶粘剂，与超过 35%-70%以上的木粉、稻壳、秸秆等废植物纤维混合成新的木质材料，再经挤压、模压、注塑成型等塑料加工工艺，生产出的板材或型材。主要用于建材、家具、物流包装等行业。将塑料和木质粉料按一定比例混合后经热挤压成型的板材，称之为挤压木塑复合板材。那么，究竟有何优点呢? 良好的加工性能 木塑复合材料内含塑料和 |
|