牌号简介 About |
---|
HIPREN® EM 1500 T是以松香酸皂为乳化剂,采用冷聚合工艺生产的,含23.5%苯乙烯的聚合物。橡胶在生产过程中加入染色抗氧化剂,使其稳定。Hipren EM 1500 T为深色,不含亚硝基胺。HIPREN® EM 1500 T与天然橡胶和其他合成橡胶兼容。良好的相容性,各种配合剂的易掺合性,为不同的应用要求提供了调配配方的可能性。用途:HIPREN® EM 1500 T用于生产各种产品,包括简单的小物件、塑压制品、轻气动和重型输送带、软管、轮胎等。 HIPREN® EM 1500 T is produced by cold copolymerisation process, with the use of rosin acids soaps as emulsifiers, and contains 23.5% styrene bounded in polymer. The rubber is stabilised with staining antioxidant added during the production process. HIPREN® EM 1500T is dark coloured, without nitrosoamine. HIPREN® EM 1500 T is compatible with natural rubber and other synthetic rubbers. Good compatibility, easy incorporation of various compounding ingredients provide possibility of mixing formulations for different applications requirement. Application: HIPREN EM 1500 T is used for production of wide range products including simple small articles, moulded and pressed products, light pneumatics and heavy conveyer belts, hoses, tires etc. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
门尼粘度 Mooney viscosity |
|||
ML 1+4,100℃ ML 1+4,100℃ |
51 | MU | ISO 289 |
结合苯乙烯 Combined with styrene |
23.5 | % | ISO 2453 |
Organic Acid Organic Acid |
6.6 | wt% | ISO 7781 |
Soap Soap |
0.5 | wt% | ISO 7781 |
Stabilizer Stabilizer |
0.4 | wt% | |
灰份含量 Ash Content |
% | ISO 247 | |
挥发物 Volatiles |
wt% | ISO 248 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness 2 |
|||
邵氏 A Shaw's A 2 |
ISO 868 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂,145℃ Fracture, 145 ℃ 2 |
MPa | ISO 37 | |
300% 应变,145℃ 300% strain, 145 ℃ 2 |
MPa | ISO 37 | |
拉伸应变 Tensile strain 2 |
|||
断裂,145℃ Fracture, 145 ℃ 2 |
% | ISO 37 | |
巴肖氏弹性 Basho's elasticity 2 |
% | ISO 4662 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
ISO 6502 | ||
50% 50% |
min | ISO 6502 | |
90% 90% |
min | ISO 6502 | |
焦化时间 Coking time |
min | ISO 6502 | |
Torque Torque |
ISO 6502 | ||
Max Max |
dNm | ISO 6502 | |
Min Min |
dNm | ISO 6502 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Vulcanization temperature 145°C; Vulcanization time 35 min; Test specimen SI |
【新闻资讯】查看全部
“欧佩克+”将灵活调整生产计划
2021-04-09 搜料网资讯: 日前,沙特阿拉伯、俄罗斯等世界主要产油国在欧佩克+月度会议上就逐步增产达成一致,决定在5月增产35万桶/日,6月在此基础上增产35万桶/日,7月再增产44.1万桶/日,除 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |