牌号简介 About |
---|
PA 6,非增强,注塑,热老化稳定,提高激光透明度,近红外激光透明着色(黑色) Durethan® B31SKH3.0LT 904040 (Dry) PA 6, non-reinforced, injection molding, heat-ageing stabilized, improved laser-transparency, NIR-laser transparent coloring (black) Durethan® B31SKH3.0LT 904040 PA 6, non-reinforced, injection molding, heat-ageing stabilized, improved laser-transparency, NIR-laser transparent coloring (black) Durethan® B31SKH3.0LT 904040 PA 6, non-reinforced, injection molding, heat-ageing stabilized, improved laser-transparency, NIR-laser transparent coloring (black) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | |
表观密度 Apparent density |
0.60 | g/cm³ | |
收缩率 Shrinkage rate |
|||
TD:120℃,2.0 mm TD:120℃,2.0 mm 2 |
0.20 | % | |
TD:270℃,2.0 mm TD:270℃,2.0 mm 3 |
1.1 | % | |
MD:120℃,2.0 mm MD:120℃,2.0 mm 2 |
0.20 | % | |
MD:270℃,2.0 mm MD:270℃,2.0 mm 3 |
% | ||
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
|||
23℃ 23℃ |
|||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-30℃ -30℃ |
kJ/m² | ||
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
|||
-30℃,冲击总贯穿能量 -30 ℃, total impact penetration energy |
J | ||
23℃,冲击总贯穿能量 23 ℃, total impact penetration energy |
J | ||
多轴向仪器化冲击力峰值 Multi axial instrumented peak impact force |
|||
-30℃ -30℃ |
N | ||
23℃ 23℃ |
N | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
维卡软化温度 Vicat Softening Temp |
℃ | ||
熔融温度 Melting temperature 6 |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ||
TD:23~55℃ TD:23~55℃ |
1/℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ||
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
球压硬度 Ball hardness |
MPa | ||
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ||
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ||
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ||
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ||
弯曲强度 bending strength 4 |
|||
23℃ 23℃ |
MPa | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ||
弯曲应变 Bending strain 5 |
% |
备注 |
---|
2. 60x60x2mm, 4 hr |
3. 60x60x2mm, 80°C MT, 600 bar |
4. 2.0 mm/min |
5. 2 mm/min |
6. 10°C/min |
【新闻资讯】查看全部
新材料!安利股份高新产品入选2022年“安徽省首批次新材料”
2022-03-20 2022年3月11日,安徽省经济和信息化厅公布《关于2022年安徽省首批次新材料名单的通知》,安利股份(300218.SZ)自主研发的高性能多功能水性无 溶剂 生态 聚氨酯复合 材料,获2022年安徽 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |