| 牌号简介 About |
|---|
| Marlex® HMN TR-935是一种中密度聚乙烯材料,。 该产品在北美洲或拉丁美洲有供货,加工方式为:滚塑成型。 Marlex® HMN TR-935的主要特性有: 阻燃/额定火焰 高抗环境应力断裂能力 (ESCR) 己烯共聚单体 良好的抗紫外线能力 耐冲击 典型应用领域包括: 水管/管道/饮用水 户外应用 农业 汽车行业 生活消费品 These hexene copolymers are tailored for rotational molding applications that require: Wide process windows Excellent impact strength Good flow Excellent ESCR Typical applications for HMN TR-935 and HMN TR-935G include items such as: Recreational and agricultural equipment Toys and carts These resins are available in: Pellet form - HMN TR-935 35 US mesh powder - HMN TR-935G These resins meet these specifications: ASTM D4976 - PE 223 FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per 21 CFR 176.170(c) Table 2. Single use articles contacting food types I, II, IV-B, VI-A, VI-B, VII-B, and VIII. Repeated use articles contacting all food types defined in 21 CFR 176.170(c) Table 1. NSF / ANSI Standard 61 for potable water (CLD 23) NSF / ANSI Standard 51 for any food contact (MTU 100°C) UL94HB yellow card per UL file E349283 UL746C (f1) yellow card per UL file E349283 FMVSS.302 burn test AS/NZS 4020:2005 (contact with drinking water) Long term UV stabilization - ASTM 2565 (Cycle 1): Greater than UV-16 |
产品描述 Product Description
用途：玩具;体育用品;农业应用;
加工条件：滚塑成型
性能特点： 防火阻燃等级HB; 己烯共聚单体; 冲击性能好; 易流动; 耐候抗UV; 抗应力开裂; HB,Good liquidity,Hexene copolymers,Weather resistance is good,High impact resistance,High ESCR
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density Density |
0.936 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Index Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
6.0 | g/10min | ASTM D1238 |
|
抗环境应力开裂 ESCR ESCR(Environmental Stress Cracking Resistance) |
ASTM D1693A | ||
|
10%非离子洗涤剂 100 % Igepal，模压成型，F50 |
130 | hr | ASTM D1693A |
|
100%非离子洗涤剂 100 % Igepal，模压成型，F50 100% non-ionic detergent, 100% Igepal, molded, F50 |
> 1000 | hr | ASTM D1693A |
|
耐候性 Weathering resistance |
f1 | UL 746C | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
ARM冲击 Impact Strength ARM Impact Strength |
|||
|
-40℃，3.20 mm -40℃，3.20 mm |
J | ||
|
-40℃，6.35 mm -40℃，6.35 mm |
J | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Heat Deflection Temperature Heat Deformation Temperature |
ASTM D648 | ||
|
0.45 MPa，未退火，3.2 mm，滚塑成型 0.45 MPa, unannealed, 3.2 mm, roll formed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火，3.17 mm，滚塑成型 1.8 MPa, unannealed, 3.17 mm, roll formed |
℃ | ASTM D648 | |
|
脆化温度 Brittleness Temperature Brittleness Temperature |
℃ | ASTM D746A | |
|
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
℃ | ASTM D1525 6 | |
|
熔融峰值温度 Melting Temperature Melting Temperature |
℃ | ASTM D3418 | |
|
结晶峰温度 Crystallization Temperature Crystallization Temperature |
|||
|
DSC DSC |
℃ | ASTM D3418 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Durometer Hardness Durometer hardness |
|||
|
邵氏 D Shore D，模压成型 Shore D, molded |
ASTM D2240 | ||
|
拉伸强度 Tensile Strength Tensile Strength |
|||
|
屈服 Yield，3.17 mm，滚塑成型 Yield, 3.17 mm, roll formed |
MPa | ASTM D638 | |
|
拉伸应变 Tensile Strain Tensile Strain |
|||
|
断裂 break，3.17 mm，滚塑成型 Break, 3.17 mm, roll formed |
% | ASTM D638 | |
|
弯曲模量 Flexural Modulus Flexural Modulus |
ASTM D790 | ||
|
2% 正割，3.17 mm，滚塑成型 2% cut, 3.17 mm, roll formed |
MPa | ASTM D790 | |
|
正切，3.17 mm，滚塑成型 Tangent, 3.17 mm, roll formed |
MPa | ASTM D790 | |
|
断裂伸长率 Elongation at Break Elongation at Break |
% | ASTM D638 | |
| 备注 |
|---|
| 1 Use conditions B through H per 21 CFR 176.170(c) Table 2. Single use articles containing food types I, II, IV-B, VI-A, VI-B, VII_B, and VIII. Repeated use articles contacting all food types defined in 21 CFR 176.170(c) Table 1. |
| 2 一般属性：这些不能被视为规格。 |
| 3 类型 4, 2.0 in/min |
| 4 0.50 in/min |
| 5 速率 A (50°C/h), 压 力1 (10N) |
|
【新闻资讯】查看全部 
三力本诺耐高温尼龙PA6T万吨级合成生产线顺利投产
2022-01-24 1月20日上午，潍坊三力本诺化学工业有限公司（以下简称三力本诺）耐高温尼龙PA6T万吨级合成生产线在山东省潍坊昌邑市龙池工业园顺利开车投产。 公开资料显示，三力本诺成立于2 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付