| 牌号简介 About |
|---|
| 概述：FZ-2130是一种30%玻璃纤维增强的线性聚苯硫醚化合物，具有良好的平衡性、优异的机械性能和加工性能。颜色：布莱克 Outline: FZ-2130 is a 30% glass fiber reinforced linear polyphenylene sulfide compound that is well balanced with excellent mechanical properties and processability. Color: Black |
产品描述 Product Description
颜色：黑色
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级V-0; 易加工; Excellent Processability,V-0
填料：玻璃纤维 30
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.56 | g/cm³ | ASTM D792 |
|
收缩率 Shrinkage rate |
ASTM D955 | ||
|
MD MD |
0.27 | % | ASTM D955 |
|
TD TD |
1.2 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
23℃，24hr 23℃，24hr |
0.020 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
90 | J/m | ASTM D256 |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM D696 | ||
|
MD：-30~90℃ MD：-30~90℃ |
1/℃ | ASTM D696 | |
|
TD：-30~90℃ TD：-30~90℃ |
1/℃ | ASTM D696 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
|||
|
1.6 mm 1.6 mm |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
|||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
|||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耐电弧性 Arc resistance |
sec | ASTM D495 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | ASTM D3638 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
0.80 mm 0.80 mm |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
|
M 级 M-level |
ASTM D785 | ||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
泊松比 Poisson's ratio |
|||
|
摩擦系数 friction coefficient 3 |
ASTM D1894 | ||
|
与钢 - 动态 Steel - Dynamic |
ASTM D1894 | ||
|
与钢 - 静态 Steel - Static |
ASTM D1894 | ||
|
断裂弯曲伸长率 Elongation at break and bending |
% | ASTM D790 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 P=150KPa, V=0.3m/s |
|
【新闻资讯】查看全部
印度持续对中国产PVC糊树脂征5年反倾销税
2016-07-11 近日，印度消费税和海关中央委员会发布公告称，接受印度商工部于2016年4月26日对原产于或进口自韩国、台湾、中国、马来西亚、泰国、俄罗斯以及欧盟的聚氯乙烯糊树脂作出的反倾销日落复审肯定性终裁结果，继续对涉案产品征收为期5年的反倾销税。中国涉案产品的反倾销税率为88公吨/美元，韩国为0～379公吨/美元，马来西亚为214公吨/美元，台湾地区为101公吨/美元，泰国为111公吨/美元，欧盟为298公吨/美元。 2009年3月31日，印度对原产于或进口自欧盟的聚氯乙烯糊/乳液树脂 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |