| 牌号简介 About |
|---|
| MAGNUM™ 555 ABS树脂是低光泽、低流动性的ABS树脂，具有6.6 ft-lb/in的板材冲击强度。Magnum ABS树脂是一种热塑性材料，可提供各种聚合物成分所赋予的加工性、抗冲击性和耐热性的极好平衡。Magnum ABS树脂有多种熔体流动速率、冲击强度和耐热性，适用于通过注塑、片材或型材挤压和热成型制造的高光泽和低光泽应用。Magnum ABS树脂的片材和热成型等级提供了优异的高光泽和低光泽美学、良好的热色稳定性、耐热和耐冲击性以及硬度。Magnum ABS树脂可满足各种需求，其熔体流动速率范围为1.0至4.0，薄板Izod冲击强度范围为2.5至10.5 ft-lb/in，薄板弯曲模量范围为285000至300000 psi。应用：墓穴衬垫工具箱休闲车行李标志符合：美国食品和药物管理局21 CFR 181.32有关完整细节，请参考法规。 MAGNUM™ 555 ABS resin is low gloss, low flow ABS resin that has a sheet Izod impact strength of 6.6 ft-lb/in. MAGNUM ABS resins are thermoplastic materials that provide an excellent balance of processability, impact resistance, and heat resistance as imparted by the various polymer compositions. MAGNUM ABS resins are available in a wide range of melt flow rates, impact strengths, and heat resistances for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion, and thermoforming. The sheet and thermoforming grades of MAGNUM ABS resins provide excellent high and low gloss aesthetics, good thermal color stability, heat and impact resistance, and stiffness. MAGNUM ABS resins can fill a variety of needs by offering ranges in melt flow rates from 1.0 to 4.0, sheet Izod impacts from 2.5 to 10.5 ft-lb/in and sheet flexural modulus from 285,000 to 300,000 psi. Applications Burial vault liners Tool cases Recreational vehicles Luggage Signs Complies with: U.S. FDA 21 CFR 181.32 Consult the regulations for complete details. |
产品描述 Product Description
用途：衬里;片材;
加工条件：型材挤出成型 Profile extrusion
性能特点： 防火阻燃等级HB; 流动性低; 机械强度好; 耐高温; 低光泽; 颜色稳定; 冲击性能好; 表面光泽度好; 易加工; Good Rigidity,Excellent Processability,Good surface appearance,Low liquidity,High impact resistance,Good color stability,High Heat Resistance,Low Gloss,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.04 | g/cm³ | ASTM D792 |
|
密度 Density |
1.05 | g/cm³ | ISO 1183-2 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，3.80kg 230℃，3.80kg |
2.4 | g/10min | ASTM D1238 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
220℃，10 kg 220℃，10 kg |
9.00 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.40 to 0.70 | % | ASTM D955 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 3 |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2 2 | |
|
拉伸强度 tensile strength 3 |
|||
|
断裂 fracture 3 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2 2 | |
|
屈服 yield 3 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield |
% | ISO 527-2 2 | |
|
Nominal strain at break Nominal strain at break |
% | ISO 527-2 2 | |
|
弯曲模量 Bending modulus 4 |
MPa | ASTM D790 | |
|
弯曲强度 bending strength 4 |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA 2 | |
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA 2 | |
|
简支梁冲击强度 Charpy impact strength |
|||
|
23℃ 23℃ |
ISO 179/1eU 2 | ||
|
-30℃ -30℃ |
ISO 179/1eU 2 | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 5 |
ASTM D256 | ||
|
-18℃，3.2mm -18℃，3.2mm |
J/m | ASTM D256 | |
|
23℃，3.2mm 23℃，3.2mm |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa 1.8 MPa |
℃ | ISO 75-2 2 | |
|
0.45 MPa 0.45 MPa |
℃ | ISO 75-2 2 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
B50 B50 |
℃ | ISO 306 2 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
1/℃ | ISO 11359-2 2 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
介电常数 Dielectric constant |
|||
|
100 Hz 100 Hz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
|||
|
100 Hz 100 Hz |
ASTM D150 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level 6 |
|||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
阻燃等级 Flame retardant level |
|||
|
1.60 mm 1.60 mm |
ISO 1210 2 | ||
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
60° 60° |
ASTM D523 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 类型 1, 2.0 in/min |
| 4 类型 1, 0.050 in/min |
| 5 10 mil 缺口深度 |
| 6 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
|
【新闻资讯】查看全部 
巴斯夫PA6 TG7S_Ultradur TG7S 供应商/物性表
2019-03-20 搜料网为你提供巴斯夫PA6 TG7S 的物性表、参考价格、材质证书、应用案例、原厂直供真货。 巴斯夫 PA6 TG7S 牌号简介： UltramidTG7S是一种34%玻璃增强，热稳定，冲击改性的PA6注塑等级。它 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付