牌号简介 About |
---|
30%玻璃纤维增强聚对苯二甲酸丁二醇酯回收含量添加“R”添加释放添加“U”用于紫外线稳定剂 30% Glass Fiber Reinforced, Polybutylene Terephthalate Recycled Content Add "R" for Added Release Add "U" for UV Stabilizer |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.50 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.30 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
117 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
3.0 | % | ASTM D638 |
弯曲模量 Bending modulus |
6210 | MPa | ASTM D790 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部 ![]()
如何防止和治理塑料净化还没有一条成功的途径
2018-08-28 目前塑料因为“白色污染”问题引起了世人的关注,但如何防止和治理塑料污染还没有一条成功的路径。 而废弃电器电子产品除了含有大量塑料外,更含有有毒有害的重金属等物质,如果处置不当,对环境造成威胁更大。在这个领域世界包含中国都已经建立了成熟的回收体系,不仅使得具有经济价值的金、银、铜等贵金属得到很好的回收再用,又能解决电子垃圾环境污染的问题。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |