牌号简介 About |
---|
聚丙烯自熄化合物,根据IEC 60335(IV版)V-2标准分类:GWFI(>850°C)E GWIT(775°C)低卤素含量,不含PBDE。不含锑和重金属,符合RoHS指令2002/95/CE。该产品在长时间暴露在外时对光具有显著的稳定性,在韧性和尺寸稳定性之间具有良好的折中性;可根据样品提供自然和彩色版本。 Polypropylene self-extinguishing compound, classifiable according to the norms of IEC 60335 (IV editions) V-2: GWFI (>850°C) e GWIT (775°C) low halogen content, free from PBDE. Free from antimony and heavy metals in agreement to RoHS directive 2002/95/CE. This product offers a remarkable stability to light for exposure of long duration to sight on the outside, and a good compromise between tenacity and dimensional stability; available in the versions natural and colored as per sample. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.925 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
15 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
1.4 | % | ISO 294-4 |
MD MD |
1.4 | % | ISO 294-4 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
无断裂 | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-40℃ -40℃ |
kJ/m² | ISO 180-1A | |
-20℃ -20℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
加速烘箱老化 Accelerate oven aging |
|||
150℃ 150℃ |
day | ISO 4577 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
球压测试 Ball pressure test |
IEC 335 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index 3 |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index 4 |
% | ISO 4589-2 | |
针焰测试 Needle flame test 5 |
|||
2.00 mm 2.00 mm 5 |
IEC 60695-2-2 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,15 秒 Shore D, 15 seconds |
ISO 868 | ||
拉伸强度 tensile strength |
ISO 527-2/20 | ||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/20 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/20 | |
拉伸应变 Tensile strain |
ISO 527-2/20 | ||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/20 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/20 | |
弯曲模量 Bending modulus 2 |
|||
23℃ 23℃ 2 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 INDONEO |
4 23°C |
5 Method A-B |
【新闻资讯】查看全部
中国工程院院士研发高强度全回收农膜
2020-12-13 搜料网资讯: 日前,高分子材料加工与机械专家、中国工程院院士瞿金平,接受CCTV-10科教频道《人物故事》栏目采访,讲述了自己如何解决残留农膜污染的问题。 瞿金平院士2013年通过 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |