牌号简介 About |
---|
PRE-ELEC® TP 11270是一种基于PE-HD的导电热塑性化合物。导电性是通过使用特殊的导电炭黑来实现的。除了低电阻率。PRE-ELEC® TP 11270具有良好的机械性能平衡,易于注塑或挤出。典型应用包括汽车燃油系统零件、挤压燃油加注管和喷射成型燃油加注管颈和头。 PRE-ELEC® TP 11270 is a conductive thermoplastic compound based on PE-HD. The electrical conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® TP 11270 has an excellent balance of mechanical properties and is easy injection mould or extrude. Typical applications include automotive fuel system parts; extruded fuel filler pipes and injection moulded fuel filler necks and heads. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
1.05 | g/cm³ | ASTM D792 |
-- -- |
1.03 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,21.6kg 190℃,21.6kg |
15 | g/10min | ASTM D1238,ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
2.5 到 3.5 | % | ASTM D955 |
MD MD |
2.5 到 3.5 | % | ISO 294-4 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 4 |
|||
-20℃ -20℃ |
kJ/m² | ISO 179 | |
-20℃ -20℃ |
kJ/m² | ASTM D256 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ASTM D256 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 4 |
ISO 179 , ASTM D256 | ||
-20℃ -20℃ |
ISO 179 , ASTM D256 | ||
23℃ 23℃ |
ISO 179 , ASTM D256 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-20℃,4mm -20℃,4mm |
kJ/m² | ASTM D256 | |
23℃,4mm 23℃,4mm |
kJ/m² | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 4 |
ISO 180 | ||
-20℃ -20℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ASTM D256 | ||
-20℃,4 mm -20℃,4 mm |
ASTM D256 | ||
23℃,4 mm 23℃,4 mm |
ASTM D256 | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 4 |
ISO 180 | ||
-20℃ -20℃ |
ISO 180 | ||
23℃ 23℃ |
ISO 180 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648-B | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648-A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 5 | |
A50 A50 |
℃ | ASTM D1525,ISO 306 | |
B50 B50 |
℃ | ISO 306 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ESD STM11.11,IEC 61340-2-3 | |
体积电阻率 Volume resistivity |
ohms·cm | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 , ISO 868 | ||
邵氏 A Shaw's A |
ASTM D2240 , ISO 868 | ||
邵氏 D Shaw's D |
ASTM D2240 , ISO 868 | ||
拉伸强度 tensile strength |
|||
MD,屈服 MD, yield |
MPa | ASTM D638 | |
TD,屈服 TD, yield |
MPa | ASTM D638 | |
MD,屈服 MD, yield |
MPa | ISO 527-2 | |
TD,屈服 TD, yield |
MPa | ISO 527-2 | |
MD MD |
MPa | ASTM D638 | |
TD TD |
MPa | ASTM D638 | |
4 mm 4 mm 2 |
MPa | ISO 527-2 | |
4 mm 4 mm 3 |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
流量,屈服 Flow rate, yield |
% | ASTM D638 , ISO 527-2 | |
TD,屈服 TD, yield |
% | ASTM D638 , ISO 527-2 | |
流量,断裂 Flow rate, fracture |
% | ASTM D638 | |
TD,断裂 TD, fracture |
% | ASTM D638 | |
断裂,4 mm Fracture, 4 mm 2 |
% | ISO 527-2 | |
断裂,0.400 mm Fracture, 0.400 mm 3 |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
4 mm 4 mm |
MPa | ASTM D790 , ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Across Flow |
3 Flow |
4 4 mm thickness |
5 标准 B (120°C/h), 载荷2 (50N) |
6 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
国际油价上涨 涨幅或受限
2021-12-08 搜料网资讯: 由于市场对新冠变异病毒奥密克戎毒株的担忧缓解和沙特提高原油售价等因素影响,国际油价6日大幅上涨,涨幅均超过4%。 截至6日收盘,纽约商品交易所2022年1月交货的轻 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |