| 牌号简介 About |
|---|
| Mold Max® XLS II是一种Shore 30A锡催化硅橡胶，具有很低的长期收缩率。XLS II型铸模在生产中比其他硅酮的耐久性更长，当铸造化学粗糙的树脂，如环氧树脂、聚酯以及聚氨酯泡沫时。配合比为100A:10B（按重量计）。在室温下，保质期为40分钟，固化时间为24小时。Mold Max® XLS II硅胶将重现最精细的细节，适用于各种工业和艺术相关应用，包括制作生产模具、复制原型、家具、雕塑和建筑元素。Mold Max® XLS II可使用THI-VEX II添加剂增稠，用于刷涂。Mold Max® XLS II硅树脂可用于浇铸各种材料，包括混凝土、蜡、石膏、低熔点合金/金属、环氧树脂或聚酯树脂（不使用脱模剂）和聚氨酯泡沫。 Mold Max® XLS® II is a Shore 30A tin-catalyzed silicone rubber that exhibits very low long-term shrinkage. XLS® II molds last longer than other silicones in production when casting chemically harsh resins such as epoxies and polyesters as well as urethane foams. Mix ratio is 100A:10B by weight. Pot life is 40 minutes and cure time is 24 hours at room temperature. Mold Max® XLS® II silicone will reproduce the finest detail and is suitable for a variety of industrial and art related applications including making production molds for, reproducing prototypes, furniture, sculpture and architectural elements. Mold Max® XLS® II can be thickened with THI-VEX® II additive for brush-on applications. Mold Max® XLS® II silicone can be used to cast a variety of materials including concrete, wax, gypsum, low melt alloys/metals, epoxy or polyester resins (without using a release agent) and urethane foams. |
产品描述 Product Description
颜色：蓝色
加工条件：浇铸 casting
性能特点： 收缩性低; Low contractility
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.22 | g/cm³ | ASTM D1475 |
|
特定体积 Specific volume |
0.820 | cm³/g | ASTM D1475 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.10 | % | ASTM D2566 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 A Shaw's A |
30 | ASTM D2240 | |
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
3.79 | MPa | ASTM D412 |
|
100% 应变 100% strain |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D412 | |
|
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
|||
|
100 Hz 100 Hz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
|||
|
100 Hz 100 Hz |
ASTM D150 | ||
|
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脱模时间 stripping time |
|||
|
23℃ 23℃ |
min | ||
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
混合比 Mixing ratio |
|||
|
工作温度 working temperature |
℃ | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM D1461 | |
|
储存稳定性 storage stability |
|||
|
23℃ 23℃ |
min | ASTM D2471 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 B 模具 |
|
【新闻资讯】查看全部 
茂名石化透明聚丙烯产品通过UL认证
2021-12-28 搜料网资讯： 近日，茂名石化透明聚丙烯系列高端产品首次通过美国UL认证。UL认证由全球检测认证机构美国UL有限公司创立，是对产品可持续性、环保、节能、降碳等性能的综合评估。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付