牌号简介 About |
---|
中分子量高密度薄膜树脂特性优异的加工性、良好的撕裂和冲击强度、良好的刚度、与低密度聚乙烯和低密度聚乙烯的良好相容性、优异的下拉性能、良好的防潮性能、应用多壁衬里、气体冲洗家禽袋、邮寄信封、重型运输袋、新鲜切割产品包老化共挤 HDPE HL 428: Excellent processability, good tear and impact strength, good stiffness, excellent compatability with LDPE and LLDPE, Excellent drawdown, good moisture barrier properties. Applications: Multi-wall liner, gas flush poultry bags, mailing envelopes, heavy-duty shipping sacks, fresh cut produce packaging, coextrusions. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.947 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.28 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
20 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
割线模量 Secant modulus |
|||
1% 正割,TD,25 µm,吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
1000 | MPa | ASTM D882A |
1% 正割,MD,25 µm,吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
MPa | ASTM D882A | |
拉伸强度 tensile strength |
ASTM D882A | ||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film 2 |
MPa | ASTM D882A | |
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ASTM D882A | |
拉伸强度 tensile strength |
ASTM D882A | ||
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film 2 |
MPa | ASTM D882A | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ASTM D882A | |
拉伸强度 tensile strength |
ASTM D882A | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film 2 |
MPa | ASTM D882A | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882A | |
拉伸强度 tensile strength |
ASTM D882A | ||
断裂,25 µm,吹塑薄膜 Fracture, 25 µ m, blown film 2 |
MPa | ASTM D882A | |
断裂,25 µm,吹塑薄膜 Fracture, 25 µ m, blown film |
MPa | ASTM D882A | |
拉伸应变 Tensile strain |
ASTM D882A | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film 2 |
% | ASTM D882A | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882A | |
拉伸应变 Tensile strain |
ASTM D882A | ||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film 2 |
% | ASTM D882A | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882A | |
落锤冲击 Drop hammer impact |
ASTM D1709A | ||
25 µm,吹塑薄膜 25 µ m, blow molded film 2 |
g | ASTM D1709-A | |
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 - MD Elmandorf Tear Strength - MD |
ASTM D1922 | ||
25 µm,吹塑薄膜 25 µ m, blow molded film 2 |
g | ASTM D1922 | |
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1922 | |
撕裂强度 tear strength |
ASTM D1922 | ||
TD,25 µm,吹塑薄膜 TD, 25 µ m, blow molded film 2 |
g | ASTM D1922 | |
TD,25 µm,吹塑薄膜 TD, 25 µ m, blow molded film |
g | ASTM D1922 | |
水气透过率 Water vapor transmittance |
ASTM F1249 | ||
25 µm,吹塑薄膜 25 µ m, blow molded film 2 |
g/m²/24 hr | ASTM F1249 | |
25 µm,吹塑薄膜 25 µ m, blow molded film |
g/m²/24 hr | ASTM F1249 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3417 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 High Stalk Extrusion |
【新闻资讯】查看全部
全球禁塑令来袭 塑料袋及相关制品替代商机凸显
2017-09-06 继中国、法国、美国、澳大利亚等40多个国家和地区相继推出禁用、部分禁止或管控塑料袋使用的政策之后,2017年8月25日,肯尼亚法院判定该国政府“禁塑令”合法有效,自8月28日起强制实施,在肯尼亚境内禁止使用、制造和进口所有用于商业和家庭用途的手提塑料袋和平底塑料袋。肯尼亚施行的这道反塑料袋法令,堪称全球最严“禁塑令”。该法令规定,生产、销售与使用塑料袋的肯尼亚公民将最高面临4年有期徒刑或约400万肯尼亚先令(约合人民币26万元)的处罚。 全球禁塑令来袭 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |