牌号简介 About |
---|
CALIBRE™ 300EP-22 聚碳酸酯树脂具有注塑模塑应用所需的优异的抗冲击性能、耐热畸变性能和光学透明度。这些产品所拥有的较高的熔体流动速率可以使其轻易地加工出复杂的零部件。CALIBRE 300 EP-22 系列产品包含有4中添加剂产品类型: CALIBRE 300EP:无脱模剂或者抗紫外线稳定剂。CALIBRE 301EP:含脱模剂。 CALIBRE 302EP:含抗紫外线稳定剂。CALIBRE 303EP:含脱模剂和抗紫外线稳定剂。 政府和业界标准: 加拿大标准协会(CSA)的要求 美国安全检测实验室 (UL)的要求 应用领域: 电器产品 存储介质 电子元器件 光散射器 CALIBRE™ 300EP-22 Series are polycarbonate resins that offer exceptional impact resistance, heat distortion resistance, and optical clarity for injection molding applications. Their high melt flow rate allows complex parts to be easily molded. The CALIBRE 300EP-22 series products are available in 4 additive packages: CALIBRE 300EP: No mold release or UV Stabilizer. CALIBRE 301EP: Mold release. CALIBRE 302EP: UV stabilizer. CALIBRE 303EP: Mold release and UV stabilizer. Govt. and Industry Standards: CSA (Canadian Standards Association) Underwriters Laboratory, Inc. (UL) Applications: Appliances Storage Electrical components Light diffusers |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ISO 1183/B |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
22 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 to 0.70 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.32 | % | ISO 62 |
23℃,24hr 23℃,24hr |
0.15 | % | ISO 62 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
球压温度 Ball pressure temperature |
℃ | IEC 60335-1 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
IEC 60250 | ||
60 Hz 60 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
50 Hz 50 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
2.00 mm,解决方案 A 2.00 mm, solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 3 |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index 3 |
IEC 60695-2-12 | ||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire 3 |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index 3 |
% | ISO 4589-2 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 2 |
MPa | ISO 178 | |
弯曲强度 bending strength 2 |
MPa | ISO 178 | |
泰伯耐磨性 Taber abraser |
% | ISO 9352 | |
洛氏硬度 Rockwell hardness |
ISO 2039-2 | ||
M 级 M-level |
ISO 2039-2 | ||
R 级 R-level |
ISO 2039-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
4 This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
【新闻资讯】查看全部
鲁南化工己内酰胺产业链一体化项目开工
2022-03-11 3月4日,山东省滕州市市委、市政府举行全市重点项目春季集中开工活动,总投资超过142亿元的22个重点项目集中开工。 鲁南化工党委书记、董事、总经理张岭介绍:为发挥链主企业牵 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |