牌号简介 About |
---|
PA 2201是一种白色的半透明聚酰胺12粉末,符合FDA,21 CFR,?77.1500 9(b),酒精食品除外。除此之外,PA 2201和PA 2200具有相同的材料性能。由PA 2201制成的激光烧结零件具有优异的材料性能:高强度和硬度、良好的耐化学性、优异的长期恒定性能、高选择性和细节分辨率、各种表面处理可能性(例如,金属化、炉搪瓷、振动研磨、桶着色、粘合、粉末涂层、植绒)。该材料的典型应用是具有最高质量的全功能塑料部件。由于其优良的力学性能,该材料经常被用来代替典型的注塑塑料。生物相容性允许其用于假体,高耐磨性允许实现可移动部件连接。 PA 2201, a whitish, a bit more translucent polyamide 12 powder, is in compliance with FDA, 21 CFR, §177.1500 9(b) except for alcoholic foodstuff. Apart from that PA 2201 and PA 2200 have identical material properties. Laser-sintered parts made from PA 2201 possess excellent material properties: high strength and stiffness good chemical resistance excellent long-term constant behaviour high selectivity and detail resolution various finishing possibilities (e.g. metallisation, stove enamelling, vibratory grinding, tub colouring, bonding, powder coating, flocking) Typical applications of the material are fully functional plastic parts of highest quality. Due to the excellent mechanical properties the material is often used to substitute typical injection moulding plastics. The biocompatibility allows its use e.g. for prostheses, the high abrasion resistance allows e.g. the realisation of movable part connections. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.930 | g/cm³ | 内部方法 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 3 |
|||
23℃ 23℃ 3 |
4.8 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 3 |
|||
23℃ 23℃ 3 |
53 | kJ/m² | ISO 179/1eU |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
4.4 | kJ/m² | ISO 180-1A |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
33 | kJ/m² | ISO 180/1U |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
熔融温度 Melting temperature 4 |
℃ | ISO 11357 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,15 秒 Shore D, 15 seconds |
ISO 868 | ||
球压硬度 Ball hardness |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus 2 |
MPa | ISO 527-2 | |
拉伸强度 tensile strength 3 |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 3 |
% | ISO 527-2 | |
弯曲模量 Bending modulus 3 |
|||
23℃ 23℃ 3 |
MPa | ISO 178 | |
弯曲强度 bending strength 3 |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 X Direction |
3 Y Direction |
4 20°C/min |
【新闻资讯】查看全部
我国首创无氯氟聚氨酯发泡剂
2018-04-19 4月15日,山东理工大学和补天新材料技术有限公司共同完成的新型无氯氟聚氨酯化学发泡剂创制项目,在北京通过中国石油和化学工业联合会组织的科技成果鉴定。由中国科学院段雪院士、中国工程院苏义脑院士领衔的鉴定委员会认为,该技术成果属国内外首创,居国际领先水平,将对我国氯氟烃发泡剂替代产生重大的推动作用。 鉴定意见显示,该技术成果具有四大创新点:一是设计合成了两类新结构无氯氟聚氨酯化学发泡剂。这两类发泡剂为化学新物质,已完成毒理实验和新物质注册,安全绿色。二是提出了新结构发泡剂的开发 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |