牌号简介 About |
---|
Xuchuan XCB-30是一种聚氨酯产品,。 它,在亚太地区有供货。 主要特性为:耐化学品。 NANCAR® 3555J is a medium high acrylonitrile butadiene copolymer with excellent oil resistance. It is polymerized at low temperature and contains sufficient antioxidant for normal aging conditions. It has fast curing rate, low mold fouling and superior resilience properties. It has good processing characteristics in compounds where flow and knitting are desired and is especially valuable in high durometer compounds. NANCAR® 3555J provides good processing and building tack. It is suggested for use in molded goods, friction stock and similar applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.00 | g/cm³ | |
门尼粘度 Mooney viscosity |
ASTM D1646 | ||
ML 1+4,100℃ ML 1+4,100℃ |
55 | MU | ASTM D1646 |
ML 1+4,100℃ ML 1+4,100℃ 2 |
71 | MU | ASTM D1646 |
丙烯腈含量(Bound) Acrylonitrile content (Bound) |
35.0 | % | 内部方法 |
Stabilizer Stabilizer |
Non-staining | ||
可溶性 solubility |
|||
in MEK in MEK |
% | ||
粘度 viscosity |
|||
最低限度 Minimum limit |
ASTM D1646 | ||
Minutes to 35 points rise,t35 Minutes to 35 points rise,t35 |
min | ||
Minutes to 5 points rise,t5 Minutes to 5 points rise,t5 |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,5 秒 Shore A, 5 seconds 3 |
ASTM D2240 | ||
邵氏 A,5 秒 Shore A, 5 seconds 4 |
ASTM D2240 | ||
邵氏 A,5 秒 Shore A, 5 seconds 5 |
ASTM D2240 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
300% 应变 300% strain 3 |
MPa | ASTM D412 | |
300% 应变 300% strain 4 |
MPa | ASTM D412 | |
300% 应变 300% strain 5 |
MPa | ASTM D412 | |
拉伸强度 tensile strength |
ASTM D412 | ||
屈服 yield 3 |
MPa | ASTM D412 | |
屈服 yield 4 |
MPa | ASTM D412 | |
屈服 yield 5 |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
ASTM D412 | ||
断裂 fracture 3 |
% | ASTM D412 | |
断裂 fracture 4 |
% | ASTM D412 | |
断裂 fracture 5 |
% | ASTM D412 | |
撕裂强度 tear strength 6 , 4 |
kN/m | ASTM D624 | |
压缩形变 Compression deformation 5 |
|||
100℃,70 hr 100℃,70 hr 5 |
% | ASTM D395 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air 7 |
|||
100℃,70 hr 100℃,70 hr 7 |
% | ASTM D573 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air 7 |
|||
100℃,70 hr 100℃,70 hr 7 |
% | ASTM D573 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air 7 |
|||
邵氏 A,100℃,70 hr Shore A, 100 ℃, 70 hr 7 |
ASTM D573 | ||
拉伸强度的变化率 The rate of change in tensile strength 7 |
ASTM D471 | ||
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在IRM 903油中 100 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
极限伸长率的变化率 Change rate of ultimate elongation 7 |
ASTM D471 | ||
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在IRM 903油中 100 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
邵氏硬度的变化率 The rate of change in Shore hardness 7 |
ASTM D471 | ||
支撐 A,100℃,70 hr,在ASTM #1油中 Support A, 100 ℃, 70 hr, in ASTM # 1 oil |
ASTM D471 | ||
支撐 A,100℃,70 hr,在IRM 903油中 Support A, 100 ℃, 70 hr, in IRM 903 oil |
ASTM D471 | ||
体积变化 Volume change 7 |
ASTM D471 | ||
100℃,70 hr,ASTM 标准油(1号) 100 ℃, 70 hr, ASTM standard oil (No.1) |
% | ASTM D471 | |
100℃,70 hr,在IRM 903油中 100 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热损耗 Heat loss |
% | ASTM D5688 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
医疗企业扎堆赴港上市 多家公司IPO折戟再递表
2022-02-22 2月21日,推想医疗科技股份有限公司(以下简称推想医疗)招股书到期,在港交所官方网站变为失效状态。 自2月14日至21日,短短一周时间,就有3家医疗公司因招股书到期导致上市折戟 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |