| 牌号简介 About |
|---|
| Viton® GBL-600S是一种新一代、易加工、过氧化固化的68%氟橡胶，基于新的先进聚合物结构技术。与原Viton GBL-900相比，Viton® GBL-600S具有可加工性，在芳烃、醇类、水、蒸汽和酸中具有类似或改进的流体阻力。与Viton GBL-900和Viton GBL-200相比，特性能快速固化到较高的固化状态，从而改善了模具的释放/污染性能，改善了模具流动性，降低了剪切敏感性，降低了65 Mooney FKM的挤出机模具膨胀，具有良好的物理性能和较高的延伸率，既有原始的，也有老化的。与Viton GBL-900和Viton GBL-200相比，TS具有相似的耐热性、耐流体性和耐低温性，在短时间（2小时）或无后固化的情况下具有优异的压缩永久变形性能。 Viton® GBL-600S is a next generation, easy processing, peroxide cured 68% fluorine fluoroelastomer based on new Advanced Polymer Architecture technology. Compared to the original Viton® GBL-900, Viton® GBL-600S exhibits processability coupled with similar or improved fluids resistance in aromatic hydrocarbons, alcohols, water, steam, and acids. Features Cures exceptionally fast to a high state of cure Exhibits improved mold release/mold fouling properties compared to Viton® GBL-900 and Viton® GBL-200 Exhibits improved mold flow, less shear sensitivity, and lower extruder die swell for a 65 Mooney FKM Exhibits excellent physical properties with high elongation, both original and aged Exhibits similar heat, fluids, and low temperature resistance compared to Viton® GBL-900 and Viton® GBL-200 Exhibits excellent compression set resistance with short (2 hr) or no postcure |
产品描述 Product Description
颜色：类白色
性能特点： 拉伸性能好; 耐酒精; 耐酸; 含脱模剂; 尺寸稳定性好; 耐碳氢化合物; 耐低温; 耐蒸汽; 易流动; 易加工; Excellent Processability,Good Dimensional Stability,Ethanol tolerance,Good liquidity,Antifreeze,Good stripping performance,Acidproof,Good Tensile Strength,Resistance to the steam,Hydrocarbons
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.84 | g/cm³ | ASTM D792 |
|
门尼粘度 Mooney viscosity |
|||
|
ML 1+10，121℃ ML 1+10，121℃ |
65 | MU | ASTM D1646 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 A，23℃ Shore A, 23 ℃ |
67 | ASTM D2240 | |
|
邵氏 A，23℃ Shore A, 23 ℃ 2 |
73 | ASTM D2240 | |
|
邵氏 A，23℃ Shore A, 23 ℃ 3 |
69 | ASTM D2240 | |
|
邵氏 A，23℃ Shore A, 23 ℃ 4 |
ASTM D2240 | ||
|
邵氏 A，23℃ Shore A, 23 ℃ 5 |
ASTM D2240 | ||
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
100% 应变，23℃ 100% strain, 23 ℃ 11 |
MPa | ASTM D412 | |
|
100% 应变，23℃ 100% strain, 23 ℃ 12 |
MPa | ASTM D412 | |
|
100% 应变，23℃ 100% strain, 23 ℃ 13 |
MPa | ASTM D412 | |
|
100% 应变，23℃ 100% strain, 23 ℃ 14 |
MPa | ASTM D412 | |
|
100% 应变，23℃ 100% strain, 23 ℃ 15 |
MPa | ASTM D412 | |
|
拉伸强度 tensile strength |
ASTM D412 | ||
|
10% 应变 10% strain |
ASTM D412 | ||
|
23℃ 23℃ 6 |
MPa | ASTM D412 | |
|
23℃ 23℃ 7 |
MPa | ASTM D412 | |
|
23℃ 23℃ 8 |
MPa | ASTM D412 | |
|
23℃ 23℃ 9 |
MPa | ASTM D412 | |
|
23℃ 23℃ 10 |
MPa | ASTM D412 | |
|
屈服，23℃ Yield, 23 ℃ 11 |
MPa | ASTM D412 | |
|
屈服，23℃ Yield, 23 ℃ 12 |
MPa | ASTM D412 | |
|
屈服，23℃ Yield, 23 ℃ 13 |
MPa | ASTM D412 | |
|
屈服，23℃ Yield, 23 ℃ 14 |
MPa | ASTM D412 | |
|
屈服，23℃ Yield, 23 ℃ 15 |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
ASTM D412 | ||
|
断裂，23℃ Fracture, 23 ℃ 11 |
% | ASTM D412 | |
|
断裂，23℃ Fracture, 23 ℃ 12 |
% | ASTM D412 | |
|
断裂，23℃ Fracture, 23 ℃ 13 |
% | ASTM D412 | |
|
断裂，23℃ Fracture, 23 ℃ 14 |
% | ASTM D412 | |
|
断裂，23℃ Fracture, 23 ℃ 15 |
% | ASTM D412 | |
|
撕裂强度 tear strength 17 |
|||
|
150℃ 150℃ 17 |
kN/m | ASTM D624 | |
|
压缩形变 Compression deformation |
ASTM D395B | ||
|
200℃，22 hr 200℃，22 hr |
% | ASTM D395B | |
|
200℃，22 hr 200℃，22 hr 18 |
% | ASTM D395B | |
|
200℃，336 hr 200℃，336 hr |
% | ASTM D395B | |
|
200℃，336 hr 200℃，336 hr 18 |
% | ASTM D395B | |
|
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积变化 Volume change |
ASTM D471 | ||
|
23℃，168 hr，C级标准燃料 23 ℃, 168 hr, C-grade standard fuel |
% | ASTM D471 | |
|
23℃，168 hr，甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
|
100℃，168 hr，在水中 100 ℃, 168 hr, in water |
% | ASTM D471 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 508 mm/min, Aged 70 hr at 275°C |
| 3 508 mm/min, Aged 168 hr at 150°C |
| 4 508 mm/min, Aged 70 hr at 250°C |
| 5 508 mm/min |
| 6 508 mm/min, Aged 2 hr at 232°C |
| 7 20 in/min |
| 8 20 in/min, 老化 168 hr 在 302°F |
| 9 20 in/min, 老化 2 hr 在 450°F |
| 10 20 in/min, 老化 70 hr 在 482°F |
| 11 20 in/min, 老化 70 hr 在 527°F |
| 12 B 模具 |
| 13 Nicked |
| 14 Postcured at 232°C |
| 15 老化 168 hr 在 302°F |
| 16 老化 2 hr 在 450°F |
| 17 老化 70 hr 在 482°F |
| 18 老化 70 hr 在 527°F |
|
【新闻资讯】查看全部 
关于2022中国（中部）工业博览会的延期通知
2022-05-12 中部工博会组委会发布公告：鉴于国内疫情防控形势严峻，经过多方商议后决定，原定于2022年5月26-28日举办的 2022中国（中部）工业博览会 延期举办， 具体日期将另行通知。详细通知 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付