| 牌号简介 About |
|---|
| Torlon 4435聚酰胺 - 酰亚胺树脂专门开发用于在高压高速(PV)环境下耐摩擦性能非常低的非润滑产品。Torlon 4435不仅特别适用于不可能进行润滑或或不需要润滑的产品，还为已经失去润滑油的润滑系统提供了额外的安全余地。 材料具有从低温到高温范围的出众的抗弯强度和抗压刚度，可用于需要承重的产品。热膨胀系数低，具有在较宽的温度范围，满足紧公差要求的能力。由于其电耗散特性，该牌号也可考虑作防静电用途。 Torlon 4435具体可用于止推垫圈、密封环、滑动叶片、线轴、衬套、离合器辊和活塞。可以注射成型为复杂形状。 高流动性：Torlon 4435-HF Torlon® 4435 is a polyamide-imide resin specifically designed to provide exceptionally low wear performance in non-lubricated applications even at high pressure and velocity (PV) conditions. Not only is Torlon® 4435 particularly suited to applications where lubrication is impossible or undesirable, it provides an additional margin of safety for lubricated systems in the event that lubrication is lost. The impressive flexural and compressive stiffness from cryogenic to elevated temperatures allows it to be used for demanding load-bearing applications. The low coefficient of thermal expansion provides the ability to meet close tolerances over a wide temperature range. Due to its electrically dissipative property, this grade may also be considered for anti-static functions. Specific applications where Torlon® 4435 may be used are thrust washers, seal rings, sliding vanes, bobbins, bushings, clutch rollers and pistons. The resin can be injection molded into complex shapes. High flow: Torlon® 4435-HF |
产品描述 Product Description
用途：密封装置;机器/机械部件;金属取代;止推垫圈;飞机应用;垫圈;轴承;汽车领域的应用;工业应用;密封件;工业部件;衬套;航空航天应用;滚轴;齿轮;传递应用;凸轮;
加工条件：注射成型 Injection Molding
性能特点： 自润滑; 耐磨; 机械强度好; 导电; 耐化学性; 耐高温; 阻燃; 低摩擦系数; 韧性好; Good Rigidity,Good flexibility,Conductive,Low coefficient of friction,Flame Characteristics,Self-lubricating,High Heat Resistance,Good wear resistance,Solvent resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.59 | g/cm³ | ASTM D792 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.14 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
24hr 24hr |
0.12 | % | ASTM D570 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
-- -- |
14500 | MPa | ASTM D638 |
|
-- -- |
9720 | MPa | ASTM D1708 |
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
MPa | ASTM D1708 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
断裂 fracture 2 |
% | ASTM D1708 | |
|
弯曲模量 Bending modulus |
ASTM D790 | ||
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
232℃ 232℃ |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
ASTM D790 | ||
|
23℃ 23℃ |
MPa | ASTM D790 | |
|
232℃ 232℃ |
MPa | ASTM D790 | |
|
压缩模量 Compression modulus |
MPa | ASTM D695 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
泊松比 Poisson's ratio |
|||
|
摩擦系数 friction coefficient |
ASTM D3702 | ||
|
-- -- 3 |
ASTM D3702 | ||
|
-- -- 4 |
ASTM D3702 | ||
|
磨损因数 Wear factor |
ASTM D3702 | ||
|
干燥： 4 m/s，0.2 MPa（800 fpm，31.25 psi） Drying: 4 m/s, 0.2 MPa (800 fpm, 31.25 psi) |
in³·min^-10/ft·lb·hr | ASTM D3702 | |
|
干燥：0.25 m/s，3.4 MPa（50 fpm，500 psi） Drying: 0.25 m/s, 3.4 MPa (50 fpm, 500 psi) |
in³·min^-10/ft·lb·hr | ASTM D3702 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
cm/cm/℃ | ASTM D696 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 以前，ASTM标准试验方法D1708用于测量PAI和类似材料的拉伸性能，因为小试样能节约更多材料。现在使用最广泛的是ASTM D638 1 Bar 试样 。所含D1708数值仅用作历史参考，不与D638值作对照用。 |
| 3 干燥： 4 m/s, 0.2 MPa (800 fpm, 31.25 psi) |
| 4 干燥：0.25 m/s, 3.4 MPa (50 fpm, 500 psi) |
|
【新闻资讯】查看全部
常用医用塑料有哪些？ 2017-09-30 7种常用的医用塑料 聚氯乙烯(pvc) 聚乙烯(PE) 聚丙烯(PP) 聚苯乙烯(PS)和K树脂 丙烯腈-丁二烯-苯乙烯(abs) 聚碳酸酯(PC) 聚四氟乙烯(PTFE) 与玻璃/金属材料相比，塑料主要特点： |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |