50-3185 NC是一种填充环氧封装材料,具有优异的物理、电气和热性能。50-3185 NC是一个很好的选择,在这里需要低热膨胀、出色的电气绝缘和/或高导热性。有三种催化剂可供选择。当用催化剂190或催化剂30固化时,该系统符合NASA的排气要求。特点:热膨胀小,绝缘性能好,导热系数高,保护和隐藏电路应用:50-3185 NC是高压应用的理想选择,如电源、变压器、高压绝缘体、套管等。 50-3185 NC is a filled epoxy encapsulant possessing excellent physical, electrical, and thermal properties. 50-3185 NC is an excellent choice where low thermal expansion, outstanding electrical insulation and/or high thermal conductivity is required. Three catalysts are available to choose from. When cured with Catalyst 190 or Catalyst 30 this system meets NASA's outgassing requirements. Features: Low Thermal Expansion Excellent Electrical Insulator High Thermal Conductivity Protects & Conceals Circuitry Applications: 50-3185 NC is ideal for high voltage applications such as power supplies, transformers, high voltage insulators, bushings, etc... |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲强度 bending strength |
124 | MPa | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
111 | ℃ | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
2.7E-5 | 1/℃ | |
导热系数 Thermal conductivity coefficient |
1.3 | W/m/K | |
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
25℃ 25℃ |
cP | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Outgassing Outgassing |
|||
冷热冲击测试 Resistance Resistance to cold and hot shock testing |
Cycles | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
重量混合比(PBW) Weight Mix Ratio (PBW) |
|||
Part A Part A |
|||
Part B Part B |
|||
密度 Density 1 |
|||
25℃ 25℃ 1 |
g/cm³ | ||
粘度 viscosity 2 |
|||
25℃ 25℃ 2 |
Pa·s | ||
固化时间 Curing time |
|||
100℃ 100℃ |
hr | ||
85℃ 85℃ |
hr | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
吸水率 Water absorption rate 3 |
% | ||
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
|||
压缩强度 compressive strength |
MPa | ||
耐电强度 Electrical strength |
kV/mm | ||
相对电容率 Relative permittivity |
|||
1 MHz 1 MHz |
|||
体积电阻率 Volume resistivity |
ohms·cm | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Mixed |
3 Part A |
4 After 24 hours |
【新闻资讯】查看全部
海南开展酵素生物降解地膜实验
2021-04-01 搜料网资讯: 海南省塑料行业协会相关人士日前表示,酵素生物降解塑料母粒可能会为塑料行业带来技术革命。 2013年以来,英国IQON公司携带其专利产品酵素生物降解塑料母粒与海南省 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-Epoxies, Ect. 50-3185 NC (Catalyst #30)证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)