牌号简介 About |
---|
ADIPRENE L 83聚氨酯橡胶是一系列聚醚基液体聚氨酯预聚物之一,通过异氰酸酯基与多胺类化合物的反应,可固化成强的橡胶固体。当用MBCA 1氨基甲酸乙酯固化剂固化时,Adiprene L 83在80-85硬度范围内生成硫化胶。ADIPRENE L 83可以铸造、压缩成型、喷涂或喷涂,以生产各种机械产品和保护性和装饰性涂层。Adiprene L 83的硫化胶提供了独特的性能组合,包括优异的耐磨性、弹性、水解稳定性和整体机械性能,使其特别适合处理矿山和磨机操作产生的研磨泥浆。用MBCA硫化的Adiprene L 83硫化胶已成功应用于采矿行业,用于生产矿浆泵、搅拌器、浮选转子和定子、旋风分离器系统、管道、阀门和筛网,以及用于旱冰和滑板轮的娱乐市场。 ADIPRENE L 83 urethane rubber is one of a series of polyether-based liquid urethane prepolymers which can be cured to a strong, rubbery solid by the reaction of the isocyanate groups with polyamine compounds. When cured with MBCA 1 urethane curative, ADIPRENE L 83 yields vulcanizates in the 80-85 durometer A hardness range. ADIPRENE L 83 can be cast, compression molded, sprayed or spread to produce a wide variety of mechanical goods and protective and decorative coatings. Vulcanizates of ADIPRENE L 83 provide a unique combination of properties including excellent abrasion resistance, resilience, hydrolytic stability and overall mechanical properties-which make it especially suitable for handling abrasive slurries from mine and mill operations. Vulcanizates of ADIPRENE L 83 cured with MBCA have been used successfuly in the mining industry to line slurry pumps, agitators, flotation rotors and stators, cyclone separator systems, piping, valves and screens, and in the recreational market for roller skate and skateboard wheels. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
1.5 | % | ASTM D955 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
100% 应变 100% strain |
4.83 | MPa | ASTM D412 |
300% 应变 300% strain |
8.27 | MPa | ASTM D412 |
拉伸强度 tensile strength |
30.3 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength |
|||
-- -- 2 |
kN/m | ASTM D624 | |
开裂 cracking |
kN/m | ASTM D470 | |
压缩形变 Compression deformation |
|||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
卡-伯模量 Kappa's modulus |
ASTM D1043 | ||
-57℃ -57℃ |
MPa | ASTM D1043 | |
-40℃ -40℃ |
MPa | ASTM D1043 | |
-18℃ -18℃ |
MPa | ASTM D1043 | |
24℃ 24℃ |
MPa | ASTM D1043 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
NBS NBS |
|||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
100℃ 100℃ |
hr | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
ASTM D797 | ||
-46℃ -46℃ |
MPa | ASTM D797 | |
-40℃ -40℃ |
MPa | ASTM D797 | |
24℃ 24℃ |
MPa | ASTM D797 | |
压缩强度 compressive strength |
ASTM D695 | ||
5% 应变 5% strain |
MPa | ASTM D695 | |
10% 应变 10% strain |
MPa | ASTM D695 | |
15% 应变 15% strain |
MPa | ASTM D695 | |
20% 应变 20% strain |
MPa | ASTM D695 | |
25% 应变 25% strain |
MPa | ASTM D695 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
储存稳定性 storage stability |
min | ||
后固化时间 Post curing time |
|||
70℃ 70℃ |
hr |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
【新闻资讯】查看全部
国务院安委办部署加强安全生产执法工作
2021-09-01 搜料网资讯: 新修改的安全生产法于9月1日起正式施行,8月31日,国务院安委会办公室召开视频会议,部署加强安全生产执法工作。 会议指出,今年以来,受新冠肺炎疫情后不稳定不确 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |