| 牌号简介 About |
|---|
| LD20-008是一种经过认证的底漆树脂，专门用于生产收缩包装吹塑薄膜，用于需要优良收缩性能、极高韧性、良好的穿刺性和耐烧性的装箱应用。LD20-008也推荐用于冲击衬膜。它具有易加工性和优良的薄膜光学和机械性能。最小推荐膜厚为1.5密耳。LD20-008不含滑块和防阻块。 LD20-008 is a certified prime resin specially designed for production of shrink wrapping Blown films for case bundling applications requiring excellent shrink performance, very high toughness, good puncture and burn-through resistance. LD20-008 is also recommended for impact liner films. It features easy processability with excellent film optical and mechanical properties. Minimum recommended film thickness is 1.5 mils. LD20-008 contains no slip and no antiblock. |
产品描述 Product Description
用途：收缩性薄膜;吹膜;
加工条件：吹塑薄膜
性能特点： 超高韧性; 低密度; 光学性能; 收缩性高; 易加工; 抗穿孔性; Excellent Processability,Optical performance,Ultra high toughness,Low density,Puncture Resistant,High shrinkage
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.922 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.80 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
38 | µm | |
|
割线模量 Secant modulus |
ASTM D882 | ||
|
1% 正割，MD：38 µm 1% secant, MD: 38 µ m |
186 | MPa | ASTM D882 |
|
1% 正割，TD：38 µm 1% secant, TD: 38 µ m |
235 | MPa | ASTM D882 |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
MD，屈服，38 µm MD, yield, 38 µ m |
MPa | ASTM D882 | |
|
TD，屈服，38 µm TD, yield, 38 µ m |
MPa | ASTM D882 | |
|
MD，断裂，38 µm MD, fracture, 38 µ m |
MPa | ASTM D882 | |
|
TD，断裂，38 µm TD, fracture, 38 µ m |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
ASTM D882 | ||
|
MD，断裂，38 µm MD, fracture, 38 µ m |
% | ASTM D882 | |
|
TD，断裂，38 µm TD, fracture, 38 µ m |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact 2 |
|||
|
25 µm 25 µm 2 |
g | ASTM D1709-A | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
|
MD：38 µm MD：38 µm |
g | ASTM D1922 | |
|
TD：38 µm TD：38 µm |
g | ASTM D1922 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，25 µm，吹塑薄膜 45 °, 25 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
25 µm，吹塑薄膜 25 µ m, blow molded film |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 F50 |
|
【新闻资讯】查看全部
福建漳州古雷炼化一体化项目奠基
2015-12-17 12月14日，福建漳州古雷炼化一体化项目奠基仪式在古雷半岛举行。十届全国人大常委会副委员长、两岸企业家峰会大陆方面副理事长盛华仁，十一届全国政协港澳台侨委员会主任陈云林，中共中央台办、国务院台办副主任龚清概，两岸企业家峰会台湾方面副理事长江丙坤，中国石化集团公司原董事长、两岸企业家峰会能源石化装备产业合作推进小组副召集人傅成玉，股份公司高级副总裁章建华、戴厚良，福建省代理省长于伟国、常务副省长张志南出席奠基仪式。 漳州古雷炼化一体化项目由大陆方面福建炼油化工有限公司和台湾方 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付