| 牌号简介 About |
|---|
| SABIC® PPcompound 5450是一种低密度改性聚丙烯。材料性能包括高流动性、高冲击性和高刚度、低收缩率和CLTE以及良好的加工能力。该材料表现出良好的美学行为，老虎条纹可见度低。典型应用包括汽车外部零件，如具有复杂和大形状的零间隙汽车保险杠应用。它可以用于喷漆和未喷漆的应用，并根据需要添加紫外线稳定。SABIC® PPcompound 5450是指定的汽车等级。 SABIC® PPcompound 5450 is a low density modified polypropylene. Material properties include very high flow, high impact and high stiffness with low shrinkage and CLTE and good process-ability. The material exhibits good esthetical behaviour with low tiger stripes visibility. Typical applications include automotive exterior parts such as zero gap automotive bumper applications with complex and large shapes. It can be used in painted and unpainted applications with UV stabilization added on demand. SABIC® PPcompound 5450 is a designated automotive grade. |
产品描述 Product Description
用途：汽车防撞杆;汽车领域的应用;汽车外部零件;
加工条件：注射成型 Injection Molding
性能特点： 机械强度好; 可表面喷涂; 流动性高; 收缩性低; 热膨胀系数低; 冲击性能好; 耐候抗UV; 低密度; 易加工; Good Rigidity,Weather resistance is good,Low CLTE,Excellent Processability,High impact resistance,High liquidity,Sprayable,Low contractility,Low density
紫外线：UV Stabilized
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.930 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
20 | g/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
24 hrs 24 hrs |
0.70 | % | 内部方法 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃，注塑成型 23 ℃, injection molding |
无断裂 | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
-40℃，注塑成型 -40 ℃, injection molding |
无断裂 | ISO 179/1eU | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/4A | ||
|
-20℃，注塑成型 -20 ℃, injection molding |
ISO 180/4A | ||
|
0℃，注塑成型 0 ℃, injection molding |
ISO 180/4A | ||
|
23℃，注塑成型 23 ℃, injection molding |
ISO 180/4A | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
ASTM D696 | ||
|
-30 到 30℃ -30 to 30 ℃ |
cm/cm/℃ | ASTM D696 | |
|
23 到 80℃ 23 to 80 ℃ |
cm/cm/℃ | ASTM D696 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D，注塑成型 Shaw's D, injection molding |
ISO 868 | ||
|
拉伸强度 tensile strength |
ISO 527-2/5/50 | ||
|
屈服，3.20 mm，注塑成型 Yield, 3.20 mm, injection molding |
MPa | ISO 527-2/5/50 | |
|
断裂，3.20 mm，注塑成型 Fracture, 3.20 mm, injection molded |
MPa | ISO 527-2/5/50 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，3.20 mm，注塑成型 Fracture, 3.20 mm, injection molded |
% | ISO 527-2/5/50 | |
|
弯曲模量 Bending modulus 2 |
|||
|
注塑成型 injection molding 2 |
MPa | ASTM D790 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 方法 I (三点负荷) |
|
【新闻资讯】查看全部
六国化工拟树立7万吨/年聚酰胺切片项目
2016-05-10 六国化工5月7日公告称，公司拟出资1亿元，设立全资子公司铜陵嘉合科技有限公司，建设7万吨/年聚酰胺切片项目。 铜陵嘉合科技有限公司注册资本1亿元，经营范围拟为化工原料(聚酰胺―6切片)的研发、生产、销售。公司表示，成立铜陵嘉合科技有限公司，主要是为了建设7万吨/年聚酰胺切片项目，该项目是公司目前煤化工产品的产业链强化和延伸，是对公司基础化工产品产业结构升级，提升生产、加工能力的尝试。 公开资料显示，聚酰胺切片具有着色性、韧性、耐磨性、自润滑性好，耐低温、耐细 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付