牌号简介 About |
---|
SABIC® PP QR674K是一种高熔体流动指数的无规共聚物,具有良好的透明性和抗静电性能。这一等级结合了改进的美学成品低温加工性和良好的感官性能。部件美观性不受较低温度的影响,从而提供更宽的操作窗口。SABICPPQR674K具有良好的流动性能、易于脱模和良好的刚度-冲击比。SABIC® PP QR674K主要用于注塑工艺。SABIC® PP QR674K的目标是透明的应用是更高的MFI的良好流动性是必需的。其预期用途包括注射成型的家庭用品、办公室和家庭储物箱、薄壁包装、盖子和盖子。本文所述产品尤其未经测试,因此未经验证可用于医药/医疗应用。 SABIC® PP QR674K is a high melt flow index random copolymer with excellent transparency and good antistatic properties. This grade combines improved aesthetics of the finished articles with low temperature processability and a very good organoleptic performance. Part aesthetics are not affected by the lower temperatures, providing for a broader operating window. The SABIC®PP QR674K presents excellent flow behaviour, easy demoulding and good stiffness to impact ratio. SABIC® PP QR674K is mainly used in injection moulding processes. The SABIC® PP QR674K aims at transparent applications were higher MFI's with good flow are required. Its intended applications include injection moulded housewares, office & home storage boxes, thin wall packaging, lids and caps & closures. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.905 | g/cm³ | ASTM D792, ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
40 | g/10min | ASTM D1238,ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
0℃ 0℃ |
2.0 | kJ/m² | |
23℃ 23℃ |
4.5 | kJ/m² | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
0℃ 0℃ |
25 | J/m | ASTM D256-A |
23℃ 23℃ |
J/m | ASTM D256-A | |
0℃ 0℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed 4 |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed 5 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525,ISO 306/A120 5 6 | |
B120 B120 |
℃ | ASTM D1525, ISO 306/B120 6 7 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
1% 正割 1% secant 1 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/1A/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/1A/50 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.039 in/min |
3 2.0 in/min |
4 testbar 80*10*4mm |
5 标准 B (120°C/h), 压 力1 (10N) |
6 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
经典再现 3D打印“复制”泰坦尼克号
2016-06-27 人类历史上最著名的沉船,非泰坦尼克号莫属了。1997年,上映同名经典爱情电影更是为这艘巨轮上演了传奇色彩。最近,模型设计师Bernard Dohnt利用3D打印技术复制了一艘可以遥控的泰坦尼克号复制品。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |