牌号简介 About |
---|
壳震快和壳震慢是一种触变塑料,混合后会自动变厚,可以刷到各种表面或橡胶模具中。当A部分和B部分按适当比例混合(体积:1a:4b或重量:1a:5b)时,材料在室温下固化,几乎没有收缩,成为一种坚硬、耐用的塑料,具有良好的压缩和弯曲强度。完全固化的铸件是刚性的,可以用砂纸打磨、涂底漆和油漆。通过添加如此强烈的色调,颜色效果是可能的。壳牌减震塑料是制作快速、轻量的刚性模具的理想选择,用于制造硅胶器具和效果(用作“石模”的替代品)。你也可以刷一个“胶衣”到一个橡胶模具,并用硬性泡沫备份,创造了一个非常详细的轻量化铸造。这些产品也可以刷到聚苯乙烯泡沫塑料(polystyrol)上,作为一种耐冲击涂层,可以打磨、涂底漆和油漆(推荐至少3层)。外壳冲击塑料也可用于制造硬支撑外壳,用于橡胶模具上的刷子。 Shell Shock® FAST and Shell Shock® SLOW are thixotropic plastics that self thicken when mixed and can be brushed onto a variety of surfaces or into rubber molds. When Parts A and B are mixed in proper proportion (1A:4B by volume or 1A:5B by weight), material cures at room temperature with virtually no shrinkage to a hard, durable plastic that exhibits good compressive and flexural strength. Fully cured castings are rigid and can be sanded, primed and painted. Color effects are possible by adding SO-Strong Color Tints. Shell Shock® plastics are ideal for making fast, lightweight rigid molds for creating silicone appliances and effects (use as a replacement for ‘stone molds'). You can also brush a "gel coat" into a rubber mold and back it up with rigid foam, creating a highly detailed lightweight casting. These products can also be brushed onto styrofoam (polystyrol) as an impact resistant coating that can be sanded, primed and painted (minimum 3 coats recommended). Shell Shock® plastics can also be used to make rigid support shells for brush on rubber molds. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.60 | g/cm³ | ASTM D1475 |
特定体积 Specific volume |
0.625 | cm³/g | ASTM D1475 |
收缩率 Shrinkage rate |
|||
MD MD |
0.060 | % | ASTM D2566 |
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脱模时间 stripping time |
|||
23℃ 23℃ |
300 | min | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
混合比 Mixing ratio |
1A:4B by volume 1A:5B by weight | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
储存稳定性 storage stability |
|||
23℃ 23℃ |
min | ASTM D2471 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
北欧化工在美国树立汽车用PP复合厂
2017-05-31 奥地利维也纳的Borealis集团决定在北卡罗莱纳州亚历山大郡的泰勒斯维尔建立专门的汽车聚丙烯(PP)复合厂。这一决定表明了北欧化工对全球汽车行业将继续履行承诺。北卡罗莱纳州的战略位置和公司的客户基础以及国家和郡的商业友好型支持环境都是此地被选中的参考因素。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |