牌号简介 About |
---|
Hifax RTA3263EUV/1分数熔体流动,1700兆帕弯曲模量,紫外线稳定,矿物填充,挤出级热塑性弹性烯烃(TEO)树脂具有良好的刚度平衡,冲击强度,耐候性和加工性。它主要设计用于挤压汽车外部轮廓应用。 Hifax RTA3263EUV/1 fractional melt flow, 1,700 MPa flexural modulus, UV-stabilized, mineral-filled, extrusion grade thermoplastic elastomeric olefin (TEO) resin has an excellent balance of stiffness, impact strength, weather resistance and processability. It was designed primarily for extruded automotive exterior profile applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.03 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
0.50 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
67 | ISO 868 | |
拉伸强度 tensile strength |
|||
屈服 yield |
23.0 | MPa | ISO 527-2 |
屈服 yield |
23.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
撕裂强度 tear strength |
kN/m | ASTM D624 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
落锤冲击 Drop hammer impact |
J | ASTM D5420 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
巴斯夫加速实施二氧化碳减排目标
2021-11-29 搜料网资讯: ●全新项目部门净零加速(Net Zero Accelerator)将由总裁齐博伦博士(Dr. Lars Kissau)领导,向集团CEO汇报 ●领导低碳技术、循环经济和可再生能源领域的跨公司项目 ●启动和 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |